Oxide dispersion strengthened CoCrFeNiMn high-entropy alloy

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F17%3A00480420" target="_blank" >RIV/68081723:_____/17:00480420 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/61389021:_____/17:00480420

Výsledek na webu

<a href="http://dx.doi.org/10.1016/j.msea.2017.02.068" target="_blank" >http://dx.doi.org/10.1016/j.msea.2017.02.068</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.msea.2017.02.068" target="_blank" >10.1016/j.msea.2017.02.068</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Oxide dispersion strengthened CoCrFeNiMn high-entropy alloy

Popis výsledku v původním jazyce

The CoCrFeNiMn high entropy alloy and its strengthened version by in-situ formed dispersion of yttria nano oxides prepared via mechanical alloying were investigated. The grain refinement of the one phase FCC alloy by presence of oxides was determined by microstructural analyses to be 50%. The positive effect of oxide dispersion on the strength properties was found to be between 30% and 70% for room and elevated temperatures, respectively. The resulting creep strain rates for the strengthened alloy were significantly lower, i.e., three orders for 30 MPa stress level, comparing the initial one, therefore, the pining mechanism was among others very effective.

Název v anglickém jazyce

Oxide dispersion strengthened CoCrFeNiMn high-entropy alloy

Popis výsledku anglicky

The CoCrFeNiMn high entropy alloy and its strengthened version by in-situ formed dispersion of yttria nano oxides prepared via mechanical alloying were investigated. The grain refinement of the one phase FCC alloy by presence of oxides was determined by microstructural analyses to be 50%. The positive effect of oxide dispersion on the strength properties was found to be between 30% and 70% for room and elevated temperatures, respectively. The resulting creep strain rates for the strengthened alloy were significantly lower, i.e., three orders for 30 MPa stress level, comparing the initial one, therefore, the pining mechanism was among others very effective.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

20501 - Materials engineering

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2017

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Materials Science and Engineering A-Structural materials

ISSN

0921-5093

e-ISSN

—

Svazek periodika

689

Číslo periodika v rámci svazku

MAR

Stát vydavatele periodika

CH - Švýcarská konfederace

Počet stran výsledku

5

Strana od-do

252-256

Kód UT WoS článku

000397698600029

EID výsledku v databázi Scopus

2-s2.0-85013482421