Influence of the Composition of the Hank’s Balanced Salt Solution on the Corrosion Behavior of AZ31 and AZ61 Magnesium Alloys

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F17%3A00481442" target="_blank" >RIV/68081723:_____/17:00481442 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/00216305:26310/17:PU125190

Výsledek na webu

<a href="http://dx.doi.org/10.3390/met7110465" target="_blank" >http://dx.doi.org/10.3390/met7110465</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.3390/met7110465" target="_blank" >10.3390/met7110465</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Influence of the Composition of the Hank’s Balanced Salt Solution on the Corrosion Behavior of AZ31 and AZ61 Magnesium Alloys

Popis výsledku v původním jazyce

The electrochemical corrosion characteristics of AZ31 and AZ61 magnesium alloys were analyzed in terms of potentiodynamic tests and electrochemical impedance spectroscopy. The influence of the solution composition and material surface finish was examined also through the analysis of corrosion products created on the samples’ surface after electrochemical measurements in terms of scanning electron microscopy using energy-dispersive spectroscopy. Obtained data revealed the differences in the response of the magnesium alloys to enriched Hank’s Balanced Salt Solution—HBSS+ (with Mg2+ and Ca2+ ions) and Hank’s Balanced Salt Solution—HBSS (without Mg2+ and Ca2+ ions). Both examined alloys exhibited better corrosion resistance from the thermodynamic and kinetic point of view in the enriched HBSS+. AZ61 magnesium alloy reached higher values of polarization resistance than AZ31 magnesium alloy in both the used corrosion solutions. Phosphate-based corrosion products were characteristic for the AZ31 and AZ61 alloys tested in the HBSS (without Mg2+ and Ca2+ ions). The combination of phosphate-based corrosion products and clusters of MgO and Mg(OH)2 was typical for the surface of samples tested in the enriched HBSS+ (with Mg2+ and Ca2+ ions). Pitting corrosion attack was observed only in the case of enriched HBSS+.

Název v anglickém jazyce

Influence of the Composition of the Hank’s Balanced Salt Solution on the Corrosion Behavior of AZ31 and AZ61 Magnesium Alloys

Popis výsledku anglicky

The electrochemical corrosion characteristics of AZ31 and AZ61 magnesium alloys were analyzed in terms of potentiodynamic tests and electrochemical impedance spectroscopy. The influence of the solution composition and material surface finish was examined also through the analysis of corrosion products created on the samples’ surface after electrochemical measurements in terms of scanning electron microscopy using energy-dispersive spectroscopy. Obtained data revealed the differences in the response of the magnesium alloys to enriched Hank’s Balanced Salt Solution—HBSS+ (with Mg2+ and Ca2+ ions) and Hank’s Balanced Salt Solution—HBSS (without Mg2+ and Ca2+ ions). Both examined alloys exhibited better corrosion resistance from the thermodynamic and kinetic point of view in the enriched HBSS+. AZ61 magnesium alloy reached higher values of polarization resistance than AZ31 magnesium alloy in both the used corrosion solutions. Phosphate-based corrosion products were characteristic for the AZ31 and AZ61 alloys tested in the HBSS (without Mg2+ and Ca2+ ions). The combination of phosphate-based corrosion products and clusters of MgO and Mg(OH)2 was typical for the surface of samples tested in the enriched HBSS+ (with Mg2+ and Ca2+ ions). Pitting corrosion attack was observed only in the case of enriched HBSS+.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

20506 - Coating and films

Projekt

<a href="/cs/project/LO1211" target="_blank" >LO1211: Centrum materiálového výzkumu na FCH VUT v Brně - udržitelnost a rozvoj</a><br>

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2017

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Metals

ISSN

2075-4701

e-ISSN

—

Svazek periodika

7

Číslo periodika v rámci svazku

11

Stát vydavatele periodika

CH - Švýcarská konfederace

Počet stran výsledku

17

Strana od-do

—

Kód UT WoS článku

000416803200015

EID výsledku v databázi Scopus

2-s2.0-85032837715