Behaviour of pre-stressed T91 and ODS steels exposed to liquid lead-bismuth eutectic

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F18%3A00491309" target="_blank" >RIV/68081723:_____/18:00491309 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/26722445:_____/18:N0000006

Výsledek na webu

<a href="http://dx.doi.org/10.1016/j.corsci.2017.12.005" target="_blank" >http://dx.doi.org/10.1016/j.corsci.2017.12.005</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.corsci.2017.12.005" target="_blank" >10.1016/j.corsci.2017.12.005</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Behaviour of pre-stressed T91 and ODS steels exposed to liquid lead-bismuth eutectic

Popis výsledku v původním jazyce

Structural materials compatibility in conditions relevant to plant operation is of primary importance to safety. The work describes the behaviour of T91 and ferritic ODS steels, 14%Cr and 19%Cr under such conditions. Three-point-bend specimens were pre-stressed up to yield strength, then exposed to flowing lead-bismuth eutectic in a loop at 350 degrees C for 500 and 1000 h, in non-flowing one for 2000 h. The oxygen content was measured to be in the order of 10(-5) wt.%. Post-test examination by means of microhardness and SEM with EDS demonstrated the formation of thin oxides without crack initiation, which is discussed. Because it was not observed either direct contact between the steels and LBE or local high plastic deformation, no LME occurred.

Název v anglickém jazyce

Behaviour of pre-stressed T91 and ODS steels exposed to liquid lead-bismuth eutectic

Popis výsledku anglicky

Structural materials compatibility in conditions relevant to plant operation is of primary importance to safety. The work describes the behaviour of T91 and ferritic ODS steels, 14%Cr and 19%Cr under such conditions. Three-point-bend specimens were pre-stressed up to yield strength, then exposed to flowing lead-bismuth eutectic in a loop at 350 degrees C for 500 and 1000 h, in non-flowing one for 2000 h. The oxygen content was measured to be in the order of 10(-5) wt.%. Post-test examination by means of microhardness and SEM with EDS demonstrated the formation of thin oxides without crack initiation, which is discussed. Because it was not observed either direct contact between the steels and LBE or local high plastic deformation, no LME occurred.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

20501 - Materials engineering

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2018

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Corrosion Science

ISSN

0010-938X

e-ISSN

—

Svazek periodika

131

Číslo periodika v rámci svazku

FEB

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

13

Strana od-do

264-277

Kód UT WoS článku

000423649800025

EID výsledku v databázi Scopus

2-s2.0-85037666482