Synergic strengthening by oxide and coherent precipitate dispersions in high-entropy alloy prepared by powder metallurgy
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F18%3A00494662" target="_blank" >RIV/68081723:_____/18:00494662 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/00216305:26210/18:PU128567
Výsledek na webu
<a href="https://www.sciencedirect.com/science/article/pii/S1359646218304536?via%3Dihub" target="_blank" >https://www.sciencedirect.com/science/article/pii/S1359646218304536?via%3Dihub</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.scriptamat.2018.07.034" target="_blank" >10.1016/j.scriptamat.2018.07.034</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Synergic strengthening by oxide and coherent precipitate dispersions in high-entropy alloy prepared by powder metallurgy
Popis výsledku v původním jazyce
The present work deals with the synthesis and evaluation of the microstructural and mechanical properties of face-centred cubic Ni1.5Co1.5CrFeTi0.5 high-entropy alloy strengthened by nano-sized titanium oxide dispersion and coherent precipitates of Ni3Ti intermetallic phase produced by powder metallurgy. The alloy's properties are well tuneable by the use of proper heat treatment. The alloy exhibits an excellent combination of tensile strength and ductility, reaching an ultimate tensile strength of 1460 MPa and elongation of 14.5% in solution annealed state and 1660MPa and 4.8% in the aged condition.Most of the strengthening contribution was attributed to Orowan-type strengthening mechanism.
Název v anglickém jazyce
Synergic strengthening by oxide and coherent precipitate dispersions in high-entropy alloy prepared by powder metallurgy
Popis výsledku anglicky
The present work deals with the synthesis and evaluation of the microstructural and mechanical properties of face-centred cubic Ni1.5Co1.5CrFeTi0.5 high-entropy alloy strengthened by nano-sized titanium oxide dispersion and coherent precipitates of Ni3Ti intermetallic phase produced by powder metallurgy. The alloy's properties are well tuneable by the use of proper heat treatment. The alloy exhibits an excellent combination of tensile strength and ductility, reaching an ultimate tensile strength of 1460 MPa and elongation of 14.5% in solution annealed state and 1660MPa and 4.8% in the aged condition.Most of the strengthening contribution was attributed to Orowan-type strengthening mechanism.
Klasifikace
Druh
J<sub>imp</sub> - Článek v periodiku v databázi Web of Science
CEP obor
—
OECD FORD obor
20501 - Materials engineering
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2018
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Scripta Materialia
ISSN
1359-6462
e-ISSN
1872-8456
Svazek periodika
157
Číslo periodika v rámci svazku
DEC
Stát vydavatele periodika
GB - Spojené království Velké Británie a Severního Irska
Počet stran výsledku
6
Strana od-do
24-29
Kód UT WoS článku
000445989500006
EID výsledku v databázi Scopus
2-s2.0-85050552309