Mechanical performance of glass-based geopolymer matrix composites reinforced with cellulose fibers

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F18%3A00500393" target="_blank" >RIV/68081723:_____/18:00500393 - isvavai.cz</a>

Výsledek na webu

<a href="http://dx.doi.org/10.3390/ma11122395" target="_blank" >http://dx.doi.org/10.3390/ma11122395</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.3390/ma11122395" target="_blank" >10.3390/ma11122395</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Mechanical performance of glass-based geopolymer matrix composites reinforced with cellulose fibers

Popis výsledku v původním jazyce

Glass-based geopolymers, incorporating fly ash and borosilicate glass, were processed in conditions of high alkalinity (NaOH 10-13 M). Different formulations (fly ash and borosilicate in mixtures of 70-30 wt% and 30-70 wt%, respectively) and physical conditions (soaking time and relative humidity) were adopted. Flexural strength and fracture toughness were assessed for samples processed in optimized conditions by three-point bending and chevron notch testing, respectively. SEM was used to evaluate the fracture micromechanisms. Results showed that the geopolymerization efficiency is strongly influenced by the SiO2/Al2O3 ratio and the curing conditions, especially the air humidity. The mechanical performances of the geopolymer samples were compared with those of cellulose fiber-geopolymer matrix composites with different fiber contents (1 wt%, 2 wt%, and 3 wt%). The composites exhibited higher strength and fracture resilience, with the maximum effect observed for the fiber content of 2 wt%. A chemical modification of the cellulose fiber surface was also observed. © 2018 by the authors.

Název v anglickém jazyce

Mechanical performance of glass-based geopolymer matrix composites reinforced with cellulose fibers

Popis výsledku anglicky

Glass-based geopolymers, incorporating fly ash and borosilicate glass, were processed in conditions of high alkalinity (NaOH 10-13 M). Different formulations (fly ash and borosilicate in mixtures of 70-30 wt% and 30-70 wt%, respectively) and physical conditions (soaking time and relative humidity) were adopted. Flexural strength and fracture toughness were assessed for samples processed in optimized conditions by three-point bending and chevron notch testing, respectively. SEM was used to evaluate the fracture micromechanisms. Results showed that the geopolymerization efficiency is strongly influenced by the SiO2/Al2O3 ratio and the curing conditions, especially the air humidity. The mechanical performances of the geopolymer samples were compared with those of cellulose fiber-geopolymer matrix composites with different fiber contents (1 wt%, 2 wt%, and 3 wt%). The composites exhibited higher strength and fracture resilience, with the maximum effect observed for the fiber content of 2 wt%. A chemical modification of the cellulose fiber surface was also observed. © 2018 by the authors.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

20505 - Composites (including laminates, reinforced plastics, cermets, combined natural and synthetic fibre fabrics; filled composites)

Projekt

—

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2018

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Materials

ISSN

1996-1944

e-ISSN

—

Svazek periodika

11

Číslo periodika v rámci svazku

12

Stát vydavatele periodika

CH - Švýcarská konfederace

Počet stran výsledku

11

Strana od-do

—

Kód UT WoS článku

000456419200053

EID výsledku v databázi Scopus

2-s2.0-85057294993