INFLUENCE OF GRAPHITE UPON THE KINETICS OF HYDROGEN SORPTION IN Mg@Mg17Al12

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F18%3A00506831" target="_blank" >RIV/68081723:_____/18:00506831 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/00216305:26620/18:PU143729

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

INFLUENCE OF GRAPHITE UPON THE KINETICS OF HYDROGEN SORPTION IN Mg@Mg17Al12

Popis výsledku v původním jazyce

Influence of graphite addition to the ball-milling charge composed of Mg splinters and Mg17Al12 particles upon the hydrogen sorption was investigated at sorption temperature 623 K. Measurements were carried out by Sieverts method. Graphite facilitates the ball-milling: It prevents re-agglomeration of crushed particles into large secondary particles. It also suppresses sticking the milled material to the balls and walls of the milling jar. It was found that an increase of carbon concentration up to a certain limit c(L) lying between 14 and 23 wt. % C, carbon increases both the absorption and the desorption rates and hydrogen storage capacity. Above c(L), carbon causes a considerable decrease in HS capacity, which spoils the application potential of Mg@Mg17Al12/C. Crystallite size of the material under study, obtained by XRD, is in the order of tens of nm.

Název v anglickém jazyce

INFLUENCE OF GRAPHITE UPON THE KINETICS OF HYDROGEN SORPTION IN Mg@Mg17Al12

Popis výsledku anglicky

Influence of graphite addition to the ball-milling charge composed of Mg splinters and Mg17Al12 particles upon the hydrogen sorption was investigated at sorption temperature 623 K. Measurements were carried out by Sieverts method. Graphite facilitates the ball-milling: It prevents re-agglomeration of crushed particles into large secondary particles. It also suppresses sticking the milled material to the balls and walls of the milling jar. It was found that an increase of carbon concentration up to a certain limit c(L) lying between 14 and 23 wt. % C, carbon increases both the absorption and the desorption rates and hydrogen storage capacity. Above c(L), carbon causes a considerable decrease in HS capacity, which spoils the application potential of Mg@Mg17Al12/C. Crystallite size of the material under study, obtained by XRD, is in the order of tens of nm.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20501 - Materials engineering

Projekt

<a href="/cs/project/GA17-21683S" target="_blank" >GA17-21683S: Kinetika ukládání vodíku v nových komplexních hydridech typu (Mg-Ni-M-S)-H</a><br>

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2018

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

9TH INTERNATIONAL CONFERENCE ON NANOMATERIALS - RESEARCH & APPLICATION (NANOCON 2017)

ISBN

978-80-87294-81-9

ISSN

—

e-ISSN

—

Počet stran výsledku

7

Strana od-do

792-798

Název nakladatele

TANGER

Místo vydání

Ostrava

Místo konání akce

Brno

Datum konání akce

18. 10. 2017

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

000452823300131