Fracture Mechanics Lifetime Prediction of Polyethylene Pipes

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F19%3A00511843" target="_blank" >RIV/68081723:_____/19:00511843 - isvavai.cz</a>

Výsledek na webu

<a href="https://ascelibrary.org/doi/full/10.1061/%28ASCE%29PS.1949-1204.0000356" target="_blank" >https://ascelibrary.org/doi/full/10.1061/%28ASCE%29PS.1949-1204.0000356</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1061/(ASCE)PS.1949-1204.0000356" target="_blank" >10.1061/(ASCE)PS.1949-1204.0000356</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Fracture Mechanics Lifetime Prediction of Polyethylene Pipes

Popis výsledku v původním jazyce

Polyethylene pressure pipes are designed for service lives of at least 50 years. While so far lifetimes have been assessed by pipe pressure testsdue to improved slow crack growth (SCG) resistance and increased testing times such tests are not suitable anymore for modern pipe grades. The paper presents an alternative methodology for lifetime prediction combining practical advantages of the cyclic cracked round bar (CRB) test and linear elastic fracture mechanics. A major advantage of this procedure is that material characterization is done at ambient temperatures. The key challenge in this context is to measure SCG rates in CRB specimens. After determination of crack kinetics at different dynamic loading ratiosmaterial laws for SCG at static loading are extrapolated. Based on the stress intensity factor concept and realistic considerations of initial defect size and changing crack front geometry pipe lifetimes of four different PE pipe grades are predicted. The results show that for all materials the required minimum lifetime of 50 years will be reached and under practical assumptions even 100 years will be exceeded. (C) 2018 American Society of Civil Engineers.

Název v anglickém jazyce

Fracture Mechanics Lifetime Prediction of Polyethylene Pipes

Popis výsledku anglicky

Polyethylene pressure pipes are designed for service lives of at least 50 years. While so far lifetimes have been assessed by pipe pressure testsdue to improved slow crack growth (SCG) resistance and increased testing times such tests are not suitable anymore for modern pipe grades. The paper presents an alternative methodology for lifetime prediction combining practical advantages of the cyclic cracked round bar (CRB) test and linear elastic fracture mechanics. A major advantage of this procedure is that material characterization is done at ambient temperatures. The key challenge in this context is to measure SCG rates in CRB specimens. After determination of crack kinetics at different dynamic loading ratiosmaterial laws for SCG at static loading are extrapolated. Based on the stress intensity factor concept and realistic considerations of initial defect size and changing crack front geometry pipe lifetimes of four different PE pipe grades are predicted. The results show that for all materials the required minimum lifetime of 50 years will be reached and under practical assumptions even 100 years will be exceeded. (C) 2018 American Society of Civil Engineers.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

20306 - Audio engineering, reliability analysis

Projekt

—

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2019

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of Pipeline Systems Engineering and Practice

ISSN

1949-1190

e-ISSN

—

Svazek periodika

10

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

US - Spojené státy americké

Počet stran výsledku

14

Strana od-do

04018030

Kód UT WoS článku

000453216800009

EID výsledku v databázi Scopus

2-s2.0-85055949411