Yield strength increase of a CoCrNi medium entropy alloy by interstitial nitrogen doping at maintained ductility

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F20%3A00524466" target="_blank" >RIV/68081723:_____/20:00524466 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/00216305:26210/19:PU135041

Výsledek na webu

<a href="https://www.sciencedirect.com/science/article/pii/S1359646219307262" target="_blank" >https://www.sciencedirect.com/science/article/pii/S1359646219307262</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.scriptamat.2019.12.007" target="_blank" >10.1016/j.scriptamat.2019.12.007</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Yield strength increase of a CoCrNi medium entropy alloy by interstitial nitrogen doping at maintained ductility

Popis výsledku v původním jazyce

We show that interstitial nitrogen doping improves the tensile properties of a CoCrNi alloy. A material with 0.5 at% interstitial nitrogen was compared to a nitrogen-free CoCrNi alloy. The nitrogen-doped variant has a stable, single-phase face-centered cubic (FCC) lattice structure without nitrides, also after different annealing treatments (800–900 °C, 10 and 30 min). The nitrogen caused an increase in yield strength by 24–33% at identical ductility compared to the nitrogen-free material with similar grain size. The strengthening effect of nitrogen was explained in terms of the simultaneous increase of the lattice friction stress and of the Hall-Petch coefficient.

Název v anglickém jazyce

Yield strength increase of a CoCrNi medium entropy alloy by interstitial nitrogen doping at maintained ductility

Popis výsledku anglicky

We show that interstitial nitrogen doping improves the tensile properties of a CoCrNi alloy. A material with 0.5 at% interstitial nitrogen was compared to a nitrogen-free CoCrNi alloy. The nitrogen-doped variant has a stable, single-phase face-centered cubic (FCC) lattice structure without nitrides, also after different annealing treatments (800–900 °C, 10 and 30 min). The nitrogen caused an increase in yield strength by 24–33% at identical ductility compared to the nitrogen-free material with similar grain size. The strengthening effect of nitrogen was explained in terms of the simultaneous increase of the lattice friction stress and of the Hall-Petch coefficient.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

20501 - Materials engineering

Projekt

—

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2020

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Scripta Materialia

ISSN

1359-6462

e-ISSN

—

Svazek periodika

178

Číslo periodika v rámci svazku

MAR

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

7

Strana od-do

391-397

Kód UT WoS článku

000510947200078

EID výsledku v databázi Scopus

2-s2.0-85076405382