Fracture and mechanical properties of lightweight alumina ceramics prepared by fused filament fabrication

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F20%3A00531335" target="_blank" >RIV/68081723:_____/20:00531335 - isvavai.cz</a>

Výsledek na webu

<a href="https://www.sciencedirect.com/science/article/pii/S0955221920301199?via%3Dihub" target="_blank" >https://www.sciencedirect.com/science/article/pii/S0955221920301199?via%3Dihub</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.jeurceramsoc.2020.02.026" target="_blank" >10.1016/j.jeurceramsoc.2020.02.026</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Fracture and mechanical properties of lightweight alumina ceramics prepared by fused filament fabrication

Popis výsledku v původním jazyce

Fused filament fabrication (FFF), as one of the additive manufacturing technology, provides cost-effective and relatively fast preparation of 3D objects of desired dimensions and design. In this work, a composite filament containing 50 vol. % of sub-micron alumina powder was successfully used for the manufacturing of samples with prismatic design. The influence of the layer thickness (0.1–0.3 mm) on the final bulk density and mechanical properties were investigated. Sintering at 1600 °C for 1 h results in relative densities ranging from 80 to 89 % and the flexural strength reached 200–300 MPa depending on the layer thickness used for the printing.

Název v anglickém jazyce

Fracture and mechanical properties of lightweight alumina ceramics prepared by fused filament fabrication

Popis výsledku anglicky

Fused filament fabrication (FFF), as one of the additive manufacturing technology, provides cost-effective and relatively fast preparation of 3D objects of desired dimensions and design. In this work, a composite filament containing 50 vol. % of sub-micron alumina powder was successfully used for the manufacturing of samples with prismatic design. The influence of the layer thickness (0.1–0.3 mm) on the final bulk density and mechanical properties were investigated. Sintering at 1600 °C for 1 h results in relative densities ranging from 80 to 89 % and the flexural strength reached 200–300 MPa depending on the layer thickness used for the printing.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

20504 - Ceramics

Projekt

—

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2020

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of the European Ceramic Society

ISSN

0955-2219

e-ISSN

—

Svazek periodika

40

Číslo periodika v rámci svazku

14

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

7

Strana od-do

4837-4843

Kód UT WoS článku

000556262000016

EID výsledku v databázi Scopus

2-s2.0-85079843784