The Role of the Surface in Crack Initiation in Sharp and Bi-material Notches

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F22%3A00565895" target="_blank" >RIV/68081723:_____/22:00565895 - isvavai.cz</a>

Výsledek na webu

<a href="http://dx.doi.org/10.1007/978-3-030-97822-8_37" target="_blank" >http://dx.doi.org/10.1007/978-3-030-97822-8_37</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1007/978-3-030-97822-8_37" target="_blank" >10.1007/978-3-030-97822-8_37</a>

Jazyk výsledku

angličtina

Název v původním jazyce

The Role of the Surface in Crack Initiation in Sharp and Bi-material Notches

Popis výsledku v původním jazyce

The study deals with description of stress distribution and conditions of crack initiation in sharp and bi-material notches. Particularly, it uses 3D numerical models of the notches and focuses on stress conditions along the notches fronts, especially near the free surface. The study describes how free surface influences the stress conditions along the notches fronts and whether crack initiates in a central or in a surface layer of the model. It can be shown that some geometries of the notches lead to crack initiation in the central layer, some of them lead to crack initiation in the surface layer, and some notches exhibit stress distribution leading to almost the same probability of crack initiation along whole notch front. The criterion of average tangential stress is used to distinguish the place of failure initiation.

Název v anglickém jazyce

The Role of the Surface in Crack Initiation in Sharp and Bi-material Notches

Popis výsledku anglicky

The study deals with description of stress distribution and conditions of crack initiation in sharp and bi-material notches. Particularly, it uses 3D numerical models of the notches and focuses on stress conditions along the notches fronts, especially near the free surface. The study describes how free surface influences the stress conditions along the notches fronts and whether crack initiates in a central or in a surface layer of the model. It can be shown that some geometries of the notches lead to crack initiation in the central layer, some of them lead to crack initiation in the surface layer, and some notches exhibit stress distribution leading to almost the same probability of crack initiation along whole notch front. The criterion of average tangential stress is used to distinguish the place of failure initiation.

Druh

C - Kapitola v odborné knize

CEP obor

—

OECD FORD obor

20302 - Applied mechanics

Projekt

<a href="/cs/project/GA20-00761S" target="_blank" >GA20-00761S: Vliv materiálových vlastností korozivzdorných ocelí na spolehlivost mostních konstrukcí</a><br>

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2022

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název knihy nebo sborníku

Structural Integrity

ISBN

978-3-030-97821-1

Počet stran výsledku

7

Strana od-do

315-321

Počet stran knihy

373

Název nakladatele

Springer Nature

Místo vydání

Berlin

Kód UT WoS kapitoly

—