Critical analysis of tig welded joint of titanium G-5 alloy sheet

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68145535%3A_____%2F15%3A00452284" target="_blank" >RIV/68145535:_____/15:00452284 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Critical analysis of tig welded joint of titanium G-5 alloy sheet

Popis výsledku v původním jazyce

Current and speed are important parameters in arc welding. This paper aims to have better understanding on the dependency of some mechanical properties of Ti-G5 alloy at micro level on welding current and speed. A Titanium G5 or Ti-6Al-4V sheet of thickness 2 mm were joined by TIG welding. Welding was carried by varying welding current and speed while keeping other parameters constant. It investigates into microstructures of different zone around the welded joint and found that microstructures become coarser near the Fusion Zone (FZ) and Heat Affected Zone (HAZ). The analysis of microhardness shows that as we move from weld centerline to base metal hardness value decreases.The thermal analysis shows that with increase in temperature the combined area of fusion zone and heat affected zone also increases.

Název v anglickém jazyce

Critical analysis of tig welded joint of titanium G-5 alloy sheet

Popis výsledku anglicky

Current and speed are important parameters in arc welding. This paper aims to have better understanding on the dependency of some mechanical properties of Ti-G5 alloy at micro level on welding current and speed. A Titanium G5 or Ti-6Al-4V sheet of thickness 2 mm were joined by TIG welding. Welding was carried by varying welding current and speed while keeping other parameters constant. It investigates into microstructures of different zone around the welded joint and found that microstructures become coarser near the Fusion Zone (FZ) and Heat Affected Zone (HAZ). The analysis of microhardness shows that as we move from weld centerline to base metal hardness value decreases.The thermal analysis shows that with increase in temperature the combined area of fusion zone and heat affected zone also increases.

Druh

D - Stať ve sborníku

CEP obor

JQ - Strojní zařízení a nástroje

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2015

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

International Scientific and Expert Conference TEAM 2015 /7./

ISBN

978-86-7083-877-2

ISSN

—

e-ISSN

—

Počet stran výsledku

5

Strana od-do

411-415

Název nakladatele

TEAM International Society, Faculty of Mechanical Engineering, University of Belgrade

Místo vydání

Belgrade

Místo konání akce

Belgrade

Datum konání akce

15. 10. 2015

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—