Erosion test with high-speed water jet applied on surface of concrete treated with solution of modified lithium silicates
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68145535%3A_____%2F19%3A00494125" target="_blank" >RIV/68145535:_____/19:00494125 - isvavai.cz</a>
Výsledek na webu
<a href="https://link.springer.com/chapter/10.1007/978-3-319-99353-9_15" target="_blank" >https://link.springer.com/chapter/10.1007/978-3-319-99353-9_15</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1007/978-3-319-99353-9_15" target="_blank" >10.1007/978-3-319-99353-9_15</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Erosion test with high-speed water jet applied on surface of concrete treated with solution of modified lithium silicates
Popis výsledku v původním jazyce
The paper focuses on the erosion resistance test based on surface treatment by a high-speed water jet applied on concrete. A reference concrete sample and concrete samples with three types of solution of modified lithium silicates applied on the concrete surface were tested under various erosion conditions. Two different jet impact angles (45° and 90°) were investigated. A significant difference in the erosion rate in the surface layers was observed comparing the untreated concrete and the concrete treated by various solutions of modified lithium silicates, but only in the initial phase of erosion.
Název v anglickém jazyce
Erosion test with high-speed water jet applied on surface of concrete treated with solution of modified lithium silicates
Popis výsledku anglicky
The paper focuses on the erosion resistance test based on surface treatment by a high-speed water jet applied on concrete. A reference concrete sample and concrete samples with three types of solution of modified lithium silicates applied on the concrete surface were tested under various erosion conditions. Two different jet impact angles (45° and 90°) were investigated. A significant difference in the erosion rate in the surface layers was observed comparing the untreated concrete and the concrete treated by various solutions of modified lithium silicates, but only in the initial phase of erosion.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
—
OECD FORD obor
20501 - Materials engineering
Návaznosti výsledku
Projekt
<a href="/cs/project/LO1406" target="_blank" >LO1406: Institut čistých technologií těžby a užití energetických surovin - Projekt udržitelnosti</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2019
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Advances in Manufacturing Engineering and Materials
ISBN
978-3-319-99353-9
ISSN
2195-4356
e-ISSN
—
Počet stran výsledku
10
Strana od-do
135-143
Název nakladatele
Springer Nature Switzerland AG 2019
Místo vydání
Basel
Místo konání akce
Nový Smokovec
Datum konání akce
18. 6. 2018
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
000462541600015