Magnetické vlastnosti nanometrických částic na bázi Fe získaných laserovou pyrolýzou plynné směsi
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F07%3A00096469" target="_blank" >RIV/68378271:_____/07:00096469 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/61388980:_____/07:00096469 RIV/68081723:_____/07:00096469
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Magnetic properties of nanometeric Fe-based particles obtained by laser-driven pyrolysis
Popis výsledku v původním jazyce
Fe-based nanoparticles were prepared by laser pyrolysis method using a cross-flow reactor in which the CO2 laser radiation orthogonally crosses with the stream of Fe(CO)5, C2H2, and C2H4 gases. The as-synthesised powder was characterised by HRTEM, XRD, Mossbauer spectroscopy, and low- and high- temperature magnetic measurements. The as-synthesised powder consisted of alpha-Fe and Fe3O4/gamma-Fe2O3 nanoparticles embedded in a pyrolytic carbon matrix. The XRD pattern of the sample exhibited broad peaks. The crystallite size d_XRD was estimated using the Scherrer formula and it was 1.8 nm for alpha-Fe and 1.6 nm for pyrolytic carbon. The as-synthesised nanopowder was superparamagnetic. The blocking temperature was determined from the maximum of the ZFC curve and it was 32 K. The Mossbauer-Lamb factor f changed strongly by cooling from 293 K to 4 K.
Název v anglickém jazyce
Magnetic properties of nanometeric Fe-based particles obtained by laser-driven pyrolysis
Popis výsledku anglicky
Fe-based nanoparticles were prepared by laser pyrolysis method using a cross-flow reactor in which the CO2 laser radiation orthogonally crosses with the stream of Fe(CO)5, C2H2, and C2H4 gases. The as-synthesised powder was characterised by HRTEM, XRD, Mossbauer spectroscopy, and low- and high- temperature magnetic measurements. The as-synthesised powder consisted of alpha-Fe and Fe3O4/gamma-Fe2O3 nanoparticles embedded in a pyrolytic carbon matrix. The XRD pattern of the sample exhibited broad peaks. The crystallite size d_XRD was estimated using the Scherrer formula and it was 1.8 nm for alpha-Fe and 1.6 nm for pyrolytic carbon. The as-synthesised nanopowder was superparamagnetic. The blocking temperature was determined from the maximum of the ZFC curve and it was 32 K. The Mossbauer-Lamb factor f changed strongly by cooling from 293 K to 4 K.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
BM - Fyzika pevných látek a magnetismus
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GA202%2F04%2F0221" target="_blank" >GA202/04/0221: Struktura, elektrické a magnetické vlastnosti nanokrystalických materiálů tvořených uhlíkem a 3d tranzitivními kovy</a><br>
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2007
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Journal of Physics and Chemistry of Solids
ISSN
0022-3697
e-ISSN
—
Svazek periodika
68
Číslo periodika v rámci svazku
5-6
Stát vydavatele periodika
GB - Spojené království Velké Británie a Severního Irska
Počet stran výsledku
5
Strana od-do
1152-1156
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—