The negative phonon confinement effect in nanoscopic sodium nitrite
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F09%3A00330274" target="_blank" >RIV/68378271:_____/09:00330274 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
The negative phonon confinement effect in nanoscopic sodium nitrite
Popis výsledku v původním jazyce
A nanocomposite of porous glass and a NaNO2 ferroelectric (channels of 7 nm diameter) was studied using infrared reflectivity, THz transmission and Raman spectroscopy as a function of temperature in the range of 300-500 K, including the ferroelectric transition. From the infrared and THz response the effective dielectric function was calculated and compared with the dielectric functions calculated from the Bruggeman and Lichtenecker models of the effective medium, using the known data on the polar phonon modes of the NaNO2 single crystals. The results show good qualitative agreement, indicating that the stiffening of the effective modes is due to local depolarization fields on the glass-ferroelectric interfaces. The nonpolar Raman modes show no substantial modification compared to those of the bulk NaNO2. Some signatures of the ferroelectric transition were even seen. The results indicate that the intrinsic size effect (phonon confinement) is negligible in this nanocomposite.
Název v anglickém jazyce
The negative phonon confinement effect in nanoscopic sodium nitrite
Popis výsledku anglicky
A nanocomposite of porous glass and a NaNO2 ferroelectric (channels of 7 nm diameter) was studied using infrared reflectivity, THz transmission and Raman spectroscopy as a function of temperature in the range of 300-500 K, including the ferroelectric transition. From the infrared and THz response the effective dielectric function was calculated and compared with the dielectric functions calculated from the Bruggeman and Lichtenecker models of the effective medium, using the known data on the polar phonon modes of the NaNO2 single crystals. The results show good qualitative agreement, indicating that the stiffening of the effective modes is due to local depolarization fields on the glass-ferroelectric interfaces. The nonpolar Raman modes show no substantial modification compared to those of the bulk NaNO2. Some signatures of the ferroelectric transition were even seen. The results indicate that the intrinsic size effect (phonon confinement) is negligible in this nanocomposite.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
BM - Fyzika pevných látek a magnetismus
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2009
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Nanotechnology
ISSN
0957-4484
e-ISSN
—
Svazek periodika
20
Číslo periodika v rámci svazku
39
Stát vydavatele periodika
GB - Spojené království Velké Británie a Severního Irska
Počet stran výsledku
7
Strana od-do
—
Kód UT WoS článku
000269553500017
EID výsledku v databázi Scopus
—