Sublattice contributions to the magnetism of UFe5Al7 and UFe6Al6.

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F10%3A00342562" target="_blank" >RIV/68378271:_____/10:00342562 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Sublattice contributions to the magnetism of UFe5Al7 and UFe6Al6.

Popis výsledku v původním jazyce

Magnetization study of intermetallic compounds UFe5Al7 and UFe6Al6 with the tetragonal crystal structure is performed on single crystals. The compounds are ferromagnets with Curie temperatures of 275 K and 315 K, respectively, and possess large magnetocrystalline anisotropy of the easy-plane type with the anisotropy field exceeding 20 T. In both UFe5Al7 and UFe6Al6, a noticeable anisotropy within the basal plane is observed with the [110] axis as the easy-magnetization direction, the [100] curve saturates in fields above 1 T. The in-plane anisotropy is the evidence for the U magnetism because it was not observed in Lu analogue. The large anisotropy persists in the paramagnetic state as well, again due to the U sublattice because it is absent in LuFe6Al6. Magnetic moments of the U and Fe atoms are estimated as 1.8 ?B and 1.3 ?B, respectively.

Název v anglickém jazyce

Sublattice contributions to the magnetism of UFe5Al7 and UFe6Al6.

Popis výsledku anglicky

Magnetization study of intermetallic compounds UFe5Al7 and UFe6Al6 with the tetragonal crystal structure is performed on single crystals. The compounds are ferromagnets with Curie temperatures of 275 K and 315 K, respectively, and possess large magnetocrystalline anisotropy of the easy-plane type with the anisotropy field exceeding 20 T. In both UFe5Al7 and UFe6Al6, a noticeable anisotropy within the basal plane is observed with the [110] axis as the easy-magnetization direction, the [100] curve saturates in fields above 1 T. The in-plane anisotropy is the evidence for the U magnetism because it was not observed in Lu analogue. The large anisotropy persists in the paramagnetic state as well, again due to the U sublattice because it is absent in LuFe6Al6. Magnetic moments of the U and Fe atoms are estimated as 1.8 ?B and 1.3 ?B, respectively.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BM - Fyzika pevných látek a magnetismus

OECD FORD obor

—

Projekt

<a href="/cs/project/GA202%2F09%2F0339" target="_blank" >GA202/09/0339: Magnetismus f-d intermetalických sloučenin</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2010

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of Alloys and Compounds

ISSN

0925-8388

e-ISSN

—

Svazek periodika

492

Číslo periodika v rámci svazku

1-2

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

4

Strana od-do

—

Kód UT WoS článku

000276018900033

EID výsledku v databázi Scopus

—