White-emitting oxidized silicon nanocrystals: Discontinuity in spectral development with reducing size

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F10%3A00343173" target="_blank" >RIV/68378271:_____/10:00343173 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

White-emitting oxidized silicon nanocrystals: Discontinuity in spectral development with reducing size

Popis výsledku v původním jazyce

Small oxidized silicon nanocrystals of average sizes below 3.5 nm are prepared using modified electrochemical etching of a silicon wafer. Modifications introduced in the etching procedure together with postetching treatment in H2O2 lead to a decrease inthe nanocrystalline core size and also, to some extent, to changes in the surface oxide. The interplay between these two factors allows us to blueshift the photoluminescence (PL) spectrum from 680 down to 590 nm, which is accompanied by changes in PL dynamics. This continual development, however, stops at about 590 nm, below which abrupt switching to fast decaying blue emission band at about 430 nm was observed. Discontinuity of the spectral shift and possible relation between both bands are discussed.

Název v anglickém jazyce

White-emitting oxidized silicon nanocrystals: Discontinuity in spectral development with reducing size

Popis výsledku anglicky

Small oxidized silicon nanocrystals of average sizes below 3.5 nm are prepared using modified electrochemical etching of a silicon wafer. Modifications introduced in the etching procedure together with postetching treatment in H2O2 lead to a decrease inthe nanocrystalline core size and also, to some extent, to changes in the surface oxide. The interplay between these two factors allows us to blueshift the photoluminescence (PL) spectrum from 680 down to 590 nm, which is accompanied by changes in PL dynamics. This continual development, however, stops at about 590 nm, below which abrupt switching to fast decaying blue emission band at about 430 nm was observed. Discontinuity of the spectral shift and possible relation between both bands are discussed.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BM - Fyzika pevných látek a magnetismus

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2010

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of Applied Physics

ISSN

0021-8979

e-ISSN

—

Svazek periodika

107

Číslo periodika v rámci svazku

5

Stát vydavatele periodika

US - Spojené státy americké

Počet stran výsledku

6

Strana od-do

—

Kód UT WoS článku

000275657500003

EID výsledku v databázi Scopus

—