Effect of ion irradiation on structure and thermal evolution of the Ni-C-60 hybrid systems

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F10%3A00346857" target="_blank" >RIV/68378271:_____/10:00346857 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/67985823:_____/10:00346857 RIV/61389005:_____/10:00346857

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Effect of ion irradiation on structure and thermal evolution of the Ni-C-60 hybrid systems

Popis výsledku v původním jazyce

We report on the thermal response of the transition metal/fullerene thin hybrid multilayers, pristine and ion-modified, i.e., Ni/C-60/Ni and Ni/a-C/Ni (a-C amorphous carbon), both prepared on the MgO(1 0 0) monocrystalline substrate. The multilayer sequences were gradually annealed up to high temperatures and their structures were inspected using several analytical techniques. The inspection evidenced differences in the evolution of the virgin and ion-irradiated systems. In pristine (non-irradiated) composites (analyzed in the previous experiment) a significant part of the fullerene molecules out-diffused during annealing < 500 degrees C. At temperatures around (and above) 500 degrees C fullerenes underwent (in the vicinity of Ni) massive fragmentationand conversion to a-C. Very high temperature (1000 degrees C) annealing resulted in the fabrication of an array of micrometer-sized octagonal pits and rod-type particles emerging from the encompassing a-C + Ni mixture.

Název v anglickém jazyce

Effect of ion irradiation on structure and thermal evolution of the Ni-C-60 hybrid systems

Popis výsledku anglicky

We report on the thermal response of the transition metal/fullerene thin hybrid multilayers, pristine and ion-modified, i.e., Ni/C-60/Ni and Ni/a-C/Ni (a-C amorphous carbon), both prepared on the MgO(1 0 0) monocrystalline substrate. The multilayer sequences were gradually annealed up to high temperatures and their structures were inspected using several analytical techniques. The inspection evidenced differences in the evolution of the virgin and ion-irradiated systems. In pristine (non-irradiated) composites (analyzed in the previous experiment) a significant part of the fullerene molecules out-diffused during annealing < 500 degrees C. At temperatures around (and above) 500 degrees C fullerenes underwent (in the vicinity of Ni) massive fragmentationand conversion to a-C. Very high temperature (1000 degrees C) annealing resulted in the fabrication of an array of micrometer-sized octagonal pits and rod-type particles emerging from the encompassing a-C + Ni mixture.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JI - Kompositní materiály

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2010

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Nuclear Instruments & Methods in Physics Research Section B

ISSN

0168-583X

e-ISSN

—

Svazek periodika

268

Číslo periodika v rámci svazku

11-12

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

4

Strana od-do

—

Kód UT WoS článku

000278702300062

EID výsledku v databázi Scopus

—