In situ TEM observation of stress-induced martensitictransformations and twinning processes in CuAlNi single crystals

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F10%3A00347975" target="_blank" >RIV/68378271:_____/10:00347975 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

In situ TEM observation of stress-induced martensitictransformations and twinning processes in CuAlNi single crystals

Popis výsledku v původním jazyce

Stress-induced martensitic transformations and twinning processes were studied in thin foils of CuAlNi single crystals strained in situ in a transmission electron microscope. The nucleation and growth of the martensite plates were monitored for three transformation processes known from bulk experiments: (i) the transformation of austenite into 2H martensite at low-stress levels; (ii) the twinning/detwinning processes in 2H martensite; and (iii) the transformation between austenite and 18R martensite athigher stress levels. The morphology of the austenite/martensite habit planes was examined, and the existence of planar interfaces between a single variant of 2H martensite and austenite on the microscopic level was proven.

Název v anglickém jazyce

In situ TEM observation of stress-induced martensitictransformations and twinning processes in CuAlNi single crystals

Popis výsledku anglicky

Stress-induced martensitic transformations and twinning processes were studied in thin foils of CuAlNi single crystals strained in situ in a transmission electron microscope. The nucleation and growth of the martensite plates were monitored for three transformation processes known from bulk experiments: (i) the transformation of austenite into 2H martensite at low-stress levels; (ii) the twinning/detwinning processes in 2H martensite; and (iii) the transformation between austenite and 18R martensite athigher stress levels. The morphology of the austenite/martensite habit planes was examined, and the existence of planar interfaces between a single variant of 2H martensite and austenite on the microscopic level was proven.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BM - Fyzika pevných látek a magnetismus

OECD FORD obor

—

Projekt

<a href="/cs/project/IAA200100627" target="_blank" >IAA200100627: Stabilita a elastické vlastnosti martenzitických fází ve slitinách s tvarovou pamětí</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2010

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Acta Materialia

ISSN

1359-6454

e-ISSN

—

Svazek periodika

58

Číslo periodika v rámci svazku

15

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

11

Strana od-do

—

Kód UT WoS článku

000280570500020

EID výsledku v databázi Scopus

—