Magnetic anisotropy of nonmodulated Ni-Mn-Ga martensite revisited

Popis výsledku v původním jazyce

Magnetic anisotropy of single crystal Ni50.5Mn30.4Ga19.1 having nonmodulated (NM) martensite structure (c=0.660 nm and b=a=0.547 nm at room temperature) was determined in the range of 10-300 K. The single variant microstructure needed for proper anisotropy determination was prepared by 40 MPa tensile stress in comparison with previous measurements where detwinned microstructure was obtained by compression. The tensile stress process yield the single variant microstructure with easy plane magnetic anisotropy and negligible second anisotropy constant in contrast of two anisotropy constants of the same order for compressed sample. The absolute value of anisotropy constant increases from 2.6x105 J/m3 at 300 K to 5x105 J/m3 at 10K.

Název v anglickém jazyce

Magnetic anisotropy of nonmodulated Ni-Mn-Ga martensite revisited

Popis výsledku anglicky

Magnetic anisotropy of single crystal Ni50.5Mn30.4Ga19.1 having nonmodulated (NM) martensite structure (c=0.660 nm and b=a=0.547 nm at room temperature) was determined in the range of 10-300 K. The single variant microstructure needed for proper anisotropy determination was prepared by 40 MPa tensile stress in comparison with previous measurements where detwinned microstructure was obtained by compression. The tensile stress process yield the single variant microstructure with easy plane magnetic anisotropy and negligible second anisotropy constant in contrast of two anisotropy constants of the same order for compressed sample. The absolute value of anisotropy constant increases from 2.6x105 J/m3 at 300 K to 5x105 J/m3 at 10K.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BM - Fyzika pevných látek a magnetismus

OECD FORD obor

—

Projekt

—

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2010

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of Applied Physics

ISSN

0021-8979

e-ISSN

—

Svazek periodika

107

Číslo periodika v rámci svazku

9

Stát vydavatele periodika

US - Spojené státy americké

Počet stran výsledku

3

Strana od-do

—

Kód UT WoS článku

000277834300119

EID výsledku v databázi Scopus

—