Structural and magnetic phase transitions in Pr0.15Sr0.85MnO3 at high pressure
Popis výsledku v původním jazyce
The crystal and magnetic structures of Pr0.15Sr0.85MnO3 manganite have been studied by means of powder X-ray and neutron diffraction in the temperature range 10?400 K at high external pressures up to 55 and 4 GPa, respectively. A structural phase transition from cubic to tetragonal phase upon compression was observed, with large positive pressure coefficient of transition temperature dTct/dP = 28(2) K/GPa. The C-type antiferromagnetic (AFM) ground state is formed below TN 260 K at ambient pressure.
Název v anglickém jazyce
Structural and magnetic phase transitions in Pr0.15Sr0.85MnO3 at high pressure
Popis výsledku anglicky
The crystal and magnetic structures of Pr0.15Sr0.85MnO3 manganite have been studied by means of powder X-ray and neutron diffraction in the temperature range 10?400 K at high external pressures up to 55 and 4 GPa, respectively. A structural phase transition from cubic to tetragonal phase upon compression was observed, with large positive pressure coefficient of transition temperature dTct/dP = 28(2) K/GPa. The C-type antiferromagnetic (AFM) ground state is formed below TN 260 K at ambient pressure.

Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
BM - Fyzika pevných látek a magnetismus
OECD FORD obor
—

Rok uplatnění
2010
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Podobné výsledky(10)