Crystal growth and VUV luminiscence properties of Er3+ - and Tm3+ -doped LiCaAlF6 for detectors

Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F10%3A00366218" target="_blank" >RIV/68378271:_____/10:00366218 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.1016/j.optmat.2010.04.032" target="_blank" >http://dx.doi.org/10.1016/j.optmat.2010.04.032</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.optmat.2010.04.032" target="_blank" >10.1016/j.optmat.2010.04.032</a>

Jazyk výsledku
angličtina
Název v původním jazyce
Crystal growth and VUV luminiscence properties of Er3+ - and Tm3+ -doped LiCaAlF6 for detectors
Popis výsledku v původním jazyce
Er- and Tm-doped LiCaAlF6 (LiCAF) single crystals were grown by the micro-pulling-down (?-PD) method. The crystals were transparent, 2,0 mm in diameter and in lenggth. Neither visible innclusions nor cracks were observed. Photoluminiscence spectra of Er-and Tm-doped LiCAF weremeasured. Broad band emission due to the Tm3+ and Er3+ 5d-4f transitions dominated the spectrum at 1635 and 16 nm respectively.
Název v anglickém jazyce
Crystal growth and VUV luminiscence properties of Er3+ - and Tm3+ -doped LiCaAlF6 for detectors
Popis výsledku anglicky
Er- and Tm-doped LiCaAlF6 (LiCAF) single crystals were grown by the micro-pulling-down (?-PD) method. The crystals were transparent, 2,0 mm in diameter and in lenggth. Neither visible innclusions nor cracks were observed. Photoluminiscence spectra of Er-and Tm-doped LiCAF weremeasured. Broad band emission due to the Tm3+ and Er3+ 5d-4f transitions dominated the spectrum at 1635 and 16 nm respectively.

Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
BM - Fyzika pevných látek a magnetismus
OECD FORD obor
—

Rok uplatnění
2010
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Podobné výsledky(10)