Crystal growth and optical properties of the Nd3+ doped LuF3 single crystals

Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F11%3A00364139" target="_blank" >RIV/68378271:_____/11:00364139 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.1016/j.optmat.2010.10.054" target="_blank" >http://dx.doi.org/10.1016/j.optmat.2010.10.054</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.optmat.2010.10.054" target="_blank" >10.1016/j.optmat.2010.10.054</a>

Jazyk výsledku
angličtina
Název v původním jazyce
Crystal growth and optical properties of the Nd3+ doped LuF3 single crystals
Popis výsledku v původním jazyce
Thirty millimeter diameter single crystal of Nd3+ doped LuF3 was grown using LiF as solvent. No remarkable absorption due to unfavorable impurities was observed from optical absorption measurements in the VUV spectral region. The crystal showed the VUV luminescence peaking around 178 nm that is consistent with the 4f25d?4f3 transition of Nd3+ ion.
Název v anglickém jazyce
Crystal growth and optical properties of the Nd3+ doped LuF3 single crystals
Popis výsledku anglicky
Thirty millimeter diameter single crystal of Nd3+ doped LuF3 was grown using LiF as solvent. No remarkable absorption due to unfavorable impurities was observed from optical absorption measurements in the VUV spectral region. The crystal showed the VUV luminescence peaking around 178 nm that is consistent with the 4f25d?4f3 transition of Nd3+ ion.

Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
BM - Fyzika pevných látek a magnetismus
OECD FORD obor
—

Rok uplatnění
2011
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Podobné výsledky(10)