Hydrogenation effect on the hysteresis properties of rapidly quenched Nd-Ho-Fe-Co-B alloys
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F11%3A00371656" target="_blank" >RIV/68378271:_____/11:00371656 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.1016/j.jallcom.2010.11.081" target="_blank" >http://dx.doi.org/10.1016/j.jallcom.2010.11.081</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.jallcom.2010.11.081" target="_blank" >10.1016/j.jallcom.2010.11.081</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Hydrogenation effect on the hysteresis properties of rapidly quenched Nd-Ho-Fe-Co-B alloys
Popis výsledku v původním jazyce
Comparative study of the rapidly-quenched (Nd0.55Ho0.45)2.7(Fe0.8Co0.2)14B1.2 alloy and its hydride has shown that hydrogenation resulted in the increase of magnetization without significant effect on the Curie temperature. In contrast to hydrogen-free alloy having a maximum on the Hc(T) curve, the Hc of the hydrogen-charged compound increased monotonously with decreasing temperature. Among the factors affecting Hc in hydrogenated sample are the increase of the grain size of the crystalline phase and the decrease of both the iron and the rare earth contributions to the magnetocrystalline anisotropy.
Název v anglickém jazyce
Hydrogenation effect on the hysteresis properties of rapidly quenched Nd-Ho-Fe-Co-B alloys
Popis výsledku anglicky
Comparative study of the rapidly-quenched (Nd0.55Ho0.45)2.7(Fe0.8Co0.2)14B1.2 alloy and its hydride has shown that hydrogenation resulted in the increase of magnetization without significant effect on the Curie temperature. In contrast to hydrogen-free alloy having a maximum on the Hc(T) curve, the Hc of the hydrogen-charged compound increased monotonously with decreasing temperature. Among the factors affecting Hc in hydrogenated sample are the increase of the grain size of the crystalline phase and the decrease of both the iron and the rare earth contributions to the magnetocrystalline anisotropy.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
BM - Fyzika pevných látek a magnetismus
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2011
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Journal of Alloys and Compounds
ISSN
0925-8388
e-ISSN
—
Svazek periodika
509
Číslo periodika v rámci svazku
2
Stát vydavatele periodika
NL - Nizozemsko
Počet stran výsledku
4
Strana od-do
"S835"-"S838"
Kód UT WoS článku
000295695500072
EID výsledku v databázi Scopus
—