Evidence of non-stoichiometry effects in nanometric manganite perovskites: influence on the magnetic ordering temperature

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F11%3A00375110" target="_blank" >RIV/68378271:_____/11:00375110 - isvavai.cz</a>

Výsledek na webu

<a href="http://dx.doi.org/10.1039/c1jm12137e" target="_blank" >http://dx.doi.org/10.1039/c1jm12137e</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1039/c1jm12137e" target="_blank" >10.1039/c1jm12137e</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Evidence of non-stoichiometry effects in nanometric manganite perovskites: influence on the magnetic ordering temperature

Popis výsledku v původním jazyce

his work tends to evidence that the significant chemical modifications observed in nanometric manganites are not concentrated at the surface of the particles and play a key role on their magnetic properties, especially for the lowest strontium-doping. La1 xSrxMnO3 solid solution with a 27 nmaverage crystallite size was prepared via the Glycine Nitrate Process. The evolutions versus x of the Curie temperature (TC) and saturation magnetization of the nanometric solid solution were interpreted taking intoaccount the Goldschmidt tolerance factor, crystallite size, amount of vacancies and the mixed valency of manganese ions.

Název v anglickém jazyce

Evidence of non-stoichiometry effects in nanometric manganite perovskites: influence on the magnetic ordering temperature

Popis výsledku anglicky

his work tends to evidence that the significant chemical modifications observed in nanometric manganites are not concentrated at the surface of the particles and play a key role on their magnetic properties, especially for the lowest strontium-doping. La1 xSrxMnO3 solid solution with a 27 nmaverage crystallite size was prepared via the Glycine Nitrate Process. The evolutions versus x of the Curie temperature (TC) and saturation magnetization of the nanometric solid solution were interpreted taking intoaccount the Goldschmidt tolerance factor, crystallite size, amount of vacancies and the mixed valency of manganese ions.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BM - Fyzika pevných látek a magnetismus

OECD FORD obor

—

Projekt

—

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2011

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of Materials Chemistry

ISSN

0959-9428

e-ISSN

—

Svazek periodika

21

Číslo periodika v rámci svazku

38

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

8

Strana od-do

14990-14998

Kód UT WoS článku

000295101000092

EID výsledku v databázi Scopus

—