Luminescence and scintillation of Ce3+- doped high silica glass

Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F12%3A00381866" target="_blank" >RIV/68378271:_____/12:00381866 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.1016/j.optmat.2012.04.012" target="_blank" >http://dx.doi.org/10.1016/j.optmat.2012.04.012</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.optmat.2012.04.012" target="_blank" >10.1016/j.optmat.2012.04.012</a>

Jazyk výsledku
angličtina
Název v původním jazyce
Luminescence and scintillation of Ce3+- doped high silica glass
Popis výsledku v původním jazyce
Ce3+- doped high silica glass was prepared by impregnation of Ce ions into a porous silica glass followed by high temperature sintering in a CO reducing atmosphere. The characteristic emission of Ce3+ 5d 4f transition peaking around 375 nm is observed inits luminescence spectra under UV and X-ray excitation. Its photoluminescence decay is governed by several tens of nanoseconds decay time. Its integral scintillation efficiency is comparable to that of a Bi4Ge3O12 (BGO) crystal under X-ray excitation. Scintillation light yield under gamma and alpha ray excitations was measured and compared with that of BGO.
Název v anglickém jazyce
Luminescence and scintillation of Ce3+- doped high silica glass
Popis výsledku anglicky
Ce3+- doped high silica glass was prepared by impregnation of Ce ions into a porous silica glass followed by high temperature sintering in a CO reducing atmosphere. The characteristic emission of Ce3+ 5d 4f transition peaking around 375 nm is observed inits luminescence spectra under UV and X-ray excitation. Its photoluminescence decay is governed by several tens of nanoseconds decay time. Its integral scintillation efficiency is comparable to that of a Bi4Ge3O12 (BGO) crystal under X-ray excitation. Scintillation light yield under gamma and alpha ray excitations was measured and compared with that of BGO.

Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
BM - Fyzika pevných látek a magnetismus
OECD FORD obor
—

Projekt
<a href="/cs/project/LH12185" target="_blank" >LH12185: Inovativní scintilátory na bázi keramik, sklo-keramik a monokrystalů: uzpůsobení materiálu a fyzikální jevy</a><br>
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění
2012
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Podobné výsledky(10)