Efficient x-ray phosphors based on non-stoichiometric MeZrO3 (Me = Ca, Sr, Ba)

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F12%3A00386362" target="_blank" >RIV/68378271:_____/12:00386362 - isvavai.cz</a>

Výsledek na webu

<a href="http://dx.doi.org/10.1109/TNS.2012.2184557" target="_blank" >http://dx.doi.org/10.1109/TNS.2012.2184557</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1109/TNS.2012.2184557" target="_blank" >10.1109/TNS.2012.2184557</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Efficient x-ray phosphors based on non-stoichiometric MeZrO3 (Me = Ca, Sr, Ba)

Popis výsledku v původním jazyce

Non-stoichiometric undoped zirconates of Ca, Sr and Ba were prepared and studied for their luminescence and scintillation characteristics in a broad range of compositions. Powder samples were prepared by solid state reaction method. Based on phase analysis the zirconate phases compositions in the sintered samples have been determined. Dominant emission band of thses materials is situated in near UV-blue spectral range. The highest scintillation efficiency was found at the samples of the strontium zirconate containing surplus of ZrO2.

Název v anglickém jazyce

Efficient x-ray phosphors based on non-stoichiometric MeZrO3 (Me = Ca, Sr, Ba)

Popis výsledku anglicky

Non-stoichiometric undoped zirconates of Ca, Sr and Ba were prepared and studied for their luminescence and scintillation characteristics in a broad range of compositions. Powder samples were prepared by solid state reaction method. Based on phase analysis the zirconate phases compositions in the sintered samples have been determined. Dominant emission band of thses materials is situated in near UV-blue spectral range. The highest scintillation efficiency was found at the samples of the strontium zirconate containing surplus of ZrO2.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BM - Fyzika pevných látek a magnetismus

OECD FORD obor

—

Projekt

<a href="/cs/project/KAN300100802" target="_blank" >KAN300100802: Nanokompositní, keramické a tenkovrstvé scintilátory</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2012

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

IEEE Transactions on Nuclear Science

ISSN

0018-9499

e-ISSN

—

Svazek periodika

59

Číslo periodika v rámci svazku

5

Stát vydavatele periodika

US - Spojené státy americké

Počet stran výsledku

7

Strana od-do

2161-2167

Kód UT WoS článku

000310143300025

EID výsledku v databázi Scopus

—