Nondestructive Magnetic Adaptive Testing of nuclear reactor pressure vessel steel degradation

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F12%3A00387734" target="_blank" >RIV/68378271:_____/12:00387734 - isvavai.cz</a>

Výsledek na webu

<a href="http://dx.doi.org/10.1016/j.jnucmat.2012.09.006" target="_blank" >http://dx.doi.org/10.1016/j.jnucmat.2012.09.006</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.jnucmat.2012.09.006" target="_blank" >10.1016/j.jnucmat.2012.09.006</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Nondestructive Magnetic Adaptive Testing of nuclear reactor pressure vessel steel degradation

Popis výsledku v původním jazyce

In this work, applicability of a novel magnetic nondestructive method (Magnetic Adaptive Testing, MAT), based on systematic measurement and evaluation of minor magnetic hysteresis loops, is shown for inspection of neutron irradiation embrittlement in nuclear reactor pressure vessel steel. Three series of samples, made of JRQ, 15CH2MFA and 10ChMFT type steels were measured by MAT. The samples were irradiated by E>1 MeV energy neutrons with total neutron fluence of 1.58*1019 ?11.9*1019 n/cm2. Regular correlation was found between the optimally chosen MAT degradation functions and the neutron fluence in all three types of the materials.

Název v anglickém jazyce

Nondestructive Magnetic Adaptive Testing of nuclear reactor pressure vessel steel degradation

Popis výsledku anglicky

In this work, applicability of a novel magnetic nondestructive method (Magnetic Adaptive Testing, MAT), based on systematic measurement and evaluation of minor magnetic hysteresis loops, is shown for inspection of neutron irradiation embrittlement in nuclear reactor pressure vessel steel. Three series of samples, made of JRQ, 15CH2MFA and 10ChMFT type steels were measured by MAT. The samples were irradiated by E>1 MeV energy neutrons with total neutron fluence of 1.58*1019 ?11.9*1019 n/cm2. Regular correlation was found between the optimally chosen MAT degradation functions and the neutron fluence in all three types of the materials.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BM - Fyzika pevných látek a magnetismus

OECD FORD obor

—

Projekt

<a href="/cs/project/GA101%2F09%2F1323" target="_blank" >GA101/09/1323: Nedestruktivní měření stavu oduhličení povrchu ocelí pomocí magnetických metod</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2012

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of Nuclear Materials

ISSN

0022-3115

e-ISSN

—

Svazek periodika

432

Číslo periodika v rámci svazku

1-3

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

7

Strana od-do

371-377

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—