Electrodynamics of (Nd,Eu,Gd)Ba2Cu3Oy single crystals

Kód výsledku v IS VaVaI

RIV/68378271:_____/12:00387786 - isvavai.cz

Nalezeny alternativní kódy

RIV/68407700:21340/12:00197989

Výsledek na webu

http://dx.doi.org/10.1016/j.phpro.2012.06.079

DOI - Digital Object Identifier

10.1016/j.phpro.2012.06.079

Jazyk výsledku

angličtina

Název v původním jazyce

Electrodynamics of (Nd,Eu,Gd)Ba2Cu3Oy single crystals

Popis výsledku v původním jazyce

ab-plane infrared spectra of two single-crystalline (Nd,Eu,Gd)Ba2Cu3Oy superconductors (NEG-123) with different Gd, Eu ratio were studied. Infrared reflectance was measured between 10 and 300 K at frequencies from 35 to 8000 cm-1. The experimental data were interpreted in terms of the two- and one-component models. The crystal with higher Gd content had more distinguished spectral features (phonons, the middle-infrared band) and about half concentration of charge carriers than the other crystal. We attribute this result to the fact that spectral features are screened by charge carriers and that the screening weakens with decreasing carrier concentration.

Název v anglickém jazyce

Electrodynamics of (Nd,Eu,Gd)Ba2Cu3Oy single crystals

Popis výsledku anglicky

ab-plane infrared spectra of two single-crystalline (Nd,Eu,Gd)Ba2Cu3Oy superconductors (NEG-123) with different Gd, Eu ratio were studied. Infrared reflectance was measured between 10 and 300 K at frequencies from 35 to 8000 cm-1. The experimental data were interpreted in terms of the two- and one-component models. The crystal with higher Gd content had more distinguished spectral features (phonons, the middle-infrared band) and about half concentration of charge carriers than the other crystal. We attribute this result to the fact that spectral features are screened by charge carriers and that the screening weakens with decreasing carrier concentration.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BM - Fyzika pevných látek a magnetismus

OECD FORD obor

—

Projekt

ME10069: Materiálové inženýrství supravodičů

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2012

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Physics Procedia

ISSN

1875-3892

e-ISSN

—

Svazek periodika

36

Číslo periodika v rámci svazku

2012

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

6

Strana od-do

532-537

Kód UT WoS článku

000314403400095

EID výsledku v databázi Scopus

—