Growth of Ce doped (Gd,Y)3Al5O12 single crystals by micro-pulling-down method and their scintillation properties

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F12%3A00556938" target="_blank" >RIV/68378271:_____/12:00556938 - isvavai.cz</a>

Výsledek na webu

<a href="https://doi.org/10.1002/pssc.201200263" target="_blank" >https://doi.org/10.1002/pssc.201200263</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1002/pssc.201200263" target="_blank" >10.1002/pssc.201200263</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Growth of Ce doped (Gd,Y)3Al5O12 single crystals by micro-pulling-down method and their scintillation properties

Popis výsledku v původním jazyce

Ce1%:(GdxY1-x)3Al5O12 (x=0, 0.2, 0.4, 0.6 and 0.8) crystals were grown by the μ-PD method. In the range of x=0~0.4, the grown crystals showed single garnet phase, but x=0.6 and 0.8 crystals showed secondary perovskite phase. In these crystals, Ce3+ 4f-5d emission was observed within 500-530 nm wavelength. Emission peaks shifted to shorter wavelength and the decay times was delayed with increasing Gd concentration. The light yield of Ce:(Gd0.6Y0.4)3Al5O12 sample was around 13,000 photon/MeV. Scintillation decay time was around 111 ns.

Název v anglickém jazyce

Growth of Ce doped (Gd,Y)3Al5O12 single crystals by micro-pulling-down method and their scintillation properties

Popis výsledku anglicky

Ce1%:(GdxY1-x)3Al5O12 (x=0, 0.2, 0.4, 0.6 and 0.8) crystals were grown by the μ-PD method. In the range of x=0~0.4, the grown crystals showed single garnet phase, but x=0.6 and 0.8 crystals showed secondary perovskite phase. In these crystals, Ce3+ 4f-5d emission was observed within 500-530 nm wavelength. Emission peaks shifted to shorter wavelength and the decay times was delayed with increasing Gd concentration. The light yield of Ce:(Gd0.6Y0.4)3Al5O12 sample was around 13,000 photon/MeV. Scintillation decay time was around 111 ns.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

10302 - Condensed matter physics (including formerly solid state physics, supercond.)

Projekt

—

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2012

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Physica Status Solidi C

ISSN

1862-6351

e-ISSN

—

Svazek periodika

9

Číslo periodika v rámci svazku

12

Stát vydavatele periodika

DE - Spolková republika Německo

Počet stran výsledku

4

Strana od-do

2292-2295

Kód UT WoS článku

000314689700017

EID výsledku v databázi Scopus

2-s2.0-84871367706