DLC coated textile vascular prostheses tested in sheep

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F13%3A00391736" target="_blank" >RIV/68378271:_____/13:00391736 - isvavai.cz</a>

Výsledek na webu

<a href="http://dx.doi.org/10.4028/www.scientific.net/AMR.647.20" target="_blank" >http://dx.doi.org/10.4028/www.scientific.net/AMR.647.20</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.4028/www.scientific.net/AMR.647.20" target="_blank" >10.4028/www.scientific.net/AMR.647.20</a>

Jazyk výsledku

angličtina

Název v původním jazyce

DLC coated textile vascular prostheses tested in sheep

Popis výsledku v původním jazyce

Textile vascular prostheses ARTECOR were coated by laser with amorphous diamondlike carbon layers (DLC) with thickness up to 200 nm. Layers were created in 0.25 Pa of Argon at laser energy density of 8 or 22 Jcm-2. Depending on the deposition conditions,DLC properties moved from soft ?graphitic? to more ?diamond? (53 % of sp3 bonds). Coated prostheses of various DLC thickness and sp3 content were implanted into carotid artery of Merino sheep. The prostheses were extirpated after 100 days (180 days). From preliminary results follows that prostheses coated with DLC layer thickness of 20 nm and higher sp3 content showed the best results.

Název v anglickém jazyce

DLC coated textile vascular prostheses tested in sheep

Popis výsledku anglicky

Textile vascular prostheses ARTECOR were coated by laser with amorphous diamondlike carbon layers (DLC) with thickness up to 200 nm. Layers were created in 0.25 Pa of Argon at laser energy density of 8 or 22 Jcm-2. Depending on the deposition conditions,DLC properties moved from soft ?graphitic? to more ?diamond? (53 % of sp3 bonds). Coated prostheses of various DLC thickness and sp3 content were implanted into carotid artery of Merino sheep. The prostheses were extirpated after 100 days (180 days). From preliminary results follows that prostheses coated with DLC layer thickness of 20 nm and higher sp3 content showed the best results.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BM - Fyzika pevných látek a magnetismus

OECD FORD obor

—

Projekt

—

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2013

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Advanced Materials Research

ISSN

1022-6680

e-ISSN

—

Svazek periodika

647

Číslo periodika v rámci svazku

JAN

Stát vydavatele periodika

CH - Švýcarská konfederace

Počet stran výsledku

5

Strana od-do

20-24

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—