Vapor phase approach for iron oxide nanoparticle synthesis from solid precursors

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F13%3A00394513" target="_blank" >RIV/68378271:_____/13:00394513 - isvavai.cz</a>

Výsledek na webu

<a href="http://dx.doi.org/10.1016/j.jssc.2013.01.037" target="_blank" >http://dx.doi.org/10.1016/j.jssc.2013.01.037</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.jssc.2013.01.037" target="_blank" >10.1016/j.jssc.2013.01.037</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Vapor phase approach for iron oxide nanoparticle synthesis from solid precursors

Popis výsledku v původním jazyce

A new non-solution mediated approach to the synthesis of iron oxide nanoparticles directly from solid FeCl2salt precursors developed. Rapid, simple and scalable method. Structural properties and the phase of the resulting iron oxide particles has been determined by a range of methods including XRD, FT-IR and Mössbauer spectroscopy, and the phase is shown to be maghemite (?-Fe2O3). Iron oxide particles magnetic properties measured using SQUID, confirming superparamagnetic behaviour of the powder and a saturation magnetization of 53.0 emu g-1 at 300 K. Aqueous dispersions at increasing concentrations prepared and their heating rate under a 400 kHz alternating magnetic field measured. The specific absorption rate (SAR) of the iron oxide was found to be 84.8 W g-1, which makes the material suitable for the formulation of ferrofluids or ferrogels with RF heating properties.

Název v anglickém jazyce

Vapor phase approach for iron oxide nanoparticle synthesis from solid precursors

Popis výsledku anglicky

A new non-solution mediated approach to the synthesis of iron oxide nanoparticles directly from solid FeCl2salt precursors developed. Rapid, simple and scalable method. Structural properties and the phase of the resulting iron oxide particles has been determined by a range of methods including XRD, FT-IR and Mössbauer spectroscopy, and the phase is shown to be maghemite (?-Fe2O3). Iron oxide particles magnetic properties measured using SQUID, confirming superparamagnetic behaviour of the powder and a saturation magnetization of 53.0 emu g-1 at 300 K. Aqueous dispersions at increasing concentrations prepared and their heating rate under a 400 kHz alternating magnetic field measured. The specific absorption rate (SAR) of the iron oxide was found to be 84.8 W g-1, which makes the material suitable for the formulation of ferrofluids or ferrogels with RF heating properties.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BM - Fyzika pevných látek a magnetismus

OECD FORD obor

—

Projekt

—

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2013

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of Solid State Chemistry

ISSN

0022-4596

e-ISSN

—

Svazek periodika

200

Číslo periodika v rámci svazku

APR

Stát vydavatele periodika

US - Spojené státy americké

Počet stran výsledku

7

Strana od-do

150-156

Kód UT WoS článku

000317158000023

EID výsledku v databázi Scopus

—