Crystal growth and characterization of calcium metaborate scintillators

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F13%3A00424358" target="_blank" >RIV/68378271:_____/13:00424358 - isvavai.cz</a>

Výsledek na webu

<a href="http://dx.doi.org/10.1016/j.nima.2012.11.002" target="_blank" >http://dx.doi.org/10.1016/j.nima.2012.11.002</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.nima.2012.11.002" target="_blank" >10.1016/j.nima.2012.11.002</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Crystal growth and characterization of calcium metaborate scintillators

Popis výsledku v původním jazyce

Calcium metaborate CaB2O4 single crystals were grown by the Czochralski(CZ)method with the radio-frequency(RF) heating system.In these crystals,a plane cleavage was observed along the growth direction. The crystals had an 80% transparency, and no absorption bands were detected in the 190?900 nm wavelength range. The 241Am 5.5MeV alpha-ray-excited radioluminescence spectrum of CaB2O4 demonstrated a broad intrinsic luminescence peak at 300?400nm, which originated from the lattice defects or an exciton-based emission. According to the pulse height spectrum, when irradiated by neutrons from a 252Cf source, the scintillation light yielded approximately 3200 photons per neutron.

Název v anglickém jazyce

Crystal growth and characterization of calcium metaborate scintillators

Popis výsledku anglicky

Calcium metaborate CaB2O4 single crystals were grown by the Czochralski(CZ)method with the radio-frequency(RF) heating system.In these crystals,a plane cleavage was observed along the growth direction. The crystals had an 80% transparency, and no absorption bands were detected in the 190?900 nm wavelength range. The 241Am 5.5MeV alpha-ray-excited radioluminescence spectrum of CaB2O4 demonstrated a broad intrinsic luminescence peak at 300?400nm, which originated from the lattice defects or an exciton-based emission. According to the pulse height spectrum, when irradiated by neutrons from a 252Cf source, the scintillation light yielded approximately 3200 photons per neutron.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BM - Fyzika pevných látek a magnetismus

OECD FORD obor

—

Projekt

—

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2013

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Nuclear Instruments & Methods in Physics Research Section A

ISSN

0168-9002

e-ISSN

—

Svazek periodika

703

Číslo periodika v rámci svazku

MAR

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

4

Strana od-do

7-10

Kód UT WoS článku

000314683700002

EID výsledku v databázi Scopus

—