Crystal growth and characterization of Ce:Gd3(Ga,Al)5O12 single crystal using floating zone method in different O2 partial pressure
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F13%3A00424792" target="_blank" >RIV/68378271:_____/13:00424792 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.1016/j.optmat.2013.02.021" target="_blank" >http://dx.doi.org/10.1016/j.optmat.2013.02.021</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.optmat.2013.02.021" target="_blank" >10.1016/j.optmat.2013.02.021</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Crystal growth and characterization of Ce:Gd3(Ga,Al)5O12 single crystal using floating zone method in different O2 partial pressure
Popis výsledku v původním jazyce
In this study, Ce:GAGG single crystals were grown by the floating zone (FZ) method under atmospheres of various compositions such as Ar 100%, Ar 80% + O2 20%, Ar 60% + O2 40% and O2 100%. Radioluminescence spectra are dominated by the band at about 540 nm due to Ce3+ 5d1?4f transition. The Ce:GAGG single crystal grown under Ar atmosphere shows an intense slower decay component. It can be related to the processes of the delayed radiative recombination and thermally induced ionization of 5d1 level of Ce3+center possibly further affected by oxygen vacancies. This slower decay process is significantly suppressed in the samples grown under the O2 containing atmosphere.
Název v anglickém jazyce
Crystal growth and characterization of Ce:Gd3(Ga,Al)5O12 single crystal using floating zone method in different O2 partial pressure
Popis výsledku anglicky
In this study, Ce:GAGG single crystals were grown by the floating zone (FZ) method under atmospheres of various compositions such as Ar 100%, Ar 80% + O2 20%, Ar 60% + O2 40% and O2 100%. Radioluminescence spectra are dominated by the band at about 540 nm due to Ce3+ 5d1?4f transition. The Ce:GAGG single crystal grown under Ar atmosphere shows an intense slower decay component. It can be related to the processes of the delayed radiative recombination and thermally induced ionization of 5d1 level of Ce3+center possibly further affected by oxygen vacancies. This slower decay process is significantly suppressed in the samples grown under the O2 containing atmosphere.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
BM - Fyzika pevných látek a magnetismus
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/LH12150" target="_blank" >LH12150: Monokrystalické a keramické scintilátory: inovativní materiálová řešení pro moderní aplikace</a><br>
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2013
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Optical Materials
ISSN
0925-3467
e-ISSN
—
Svazek periodika
35
Číslo periodika v rámci svazku
11
Stát vydavatele periodika
NL - Nizozemsko
Počet stran výsledku
5
Strana od-do
1882-1886
Kód UT WoS článku
000324962500003
EID výsledku v databázi Scopus
—