Magneto-structural transitions induced at 1.2 K in Ni2MnGa-based Heusler alloys by high magnetic field up to 60 T

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F14%3A00427380" target="_blank" >RIV/68378271:_____/14:00427380 - isvavai.cz</a>

Výsledek na webu

<a href="http://dx.doi.org/10.1088/2053-1591/1/1/016109" target="_blank" >http://dx.doi.org/10.1088/2053-1591/1/1/016109</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1088/2053-1591/1/1/016109" target="_blank" >10.1088/2053-1591/1/1/016109</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Magneto-structural transitions induced at 1.2 K in Ni2MnGa-based Heusler alloys by high magnetic field up to 60 T

Popis výsledku v původním jazyce

The huge decrease of the martensitic transition temperature TM-A with increasing field (up to dTM-A/dH=8.1 K T-1) was observed in all the Co-doped and In-doped Ni50-xCoxMn25+yGa25-y-zInz Heusler alloys at high pulse magnetic field up to 60 T. The structural martensitic transitions were induced at temperatures 2 K and 1.2 K in the Ni1.72Co0.28Mn1.25Ga0.75 and Ni1.65Co0.34Mn1.31Ga0.62In0.07 alloys, respectively.The transitions are accompanied by a significant increase of magnetization of their austenite phase with increasing field up to MA(2 K)=6.3?B/f

Název v anglickém jazyce

Magneto-structural transitions induced at 1.2 K in Ni2MnGa-based Heusler alloys by high magnetic field up to 60 T

Popis výsledku anglicky

The huge decrease of the martensitic transition temperature TM-A with increasing field (up to dTM-A/dH=8.1 K T-1) was observed in all the Co-doped and In-doped Ni50-xCoxMn25+yGa25-y-zInz Heusler alloys at high pulse magnetic field up to 60 T. The structural martensitic transitions were induced at temperatures 2 K and 1.2 K in the Ni1.72Co0.28Mn1.25Ga0.75 and Ni1.65Co0.34Mn1.31Ga0.62In0.07 alloys, respectively.The transitions are accompanied by a significant increase of magnetization of their austenite phase with increasing field up to MA(2 K)=6.3?B/f

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BM - Fyzika pevných látek a magnetismus

OECD FORD obor

—

Projekt

—

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2014

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Materials Research Express

ISSN

2053-1591

e-ISSN

—

Svazek periodika

1

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

8

Strana od-do

1-7

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—