Crystal growth, optical spectroscopy, and continuous-wave laser operation of co-doped (Ho, Tm):KLu(WO4)2 monoclinic crystals

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F14%3A00510573" target="_blank" >RIV/68378271:_____/14:00510573 - isvavai.cz</a>

Výsledek na webu

<a href="https://doi.org/10.1364/josab.31.001415" target="_blank" >https://doi.org/10.1364/josab.31.001415</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1364/JOSAB.31.001415" target="_blank" >10.1364/JOSAB.31.001415</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Crystal growth, optical spectroscopy, and continuous-wave laser operation of co-doped (Ho, Tm):KLu(WO4)2 monoclinic crystals

Popis výsledku v původním jazyce

We report on the crystal growth, optical spectroscopy, and room-temperature continuous-wave laser generation around 2 μm with co-doped Ho, Tm∶KLu WO42 monoclinic crystals. Co-doped crystals at different doping levels were grown by the top-seeded solution growth slow-cooling method. We characterized the spectroscopy of Ho and Tm ions in KLuW in terms of polarized optical absorption, photoluminescence, and lifetime measurements. Continuous-wave laser operation at room-temperature at a wavelength of 2.06 μm was achieved with several crystals at different co-doping levels, establishing that the optimum doping ratio is 5.29 × 1019 at:∕cm3 for Ho and 3.10 × 1020 at:∕cm3 for Tm (0.5 at. %Ho, 5.0 at. %Tm:KLuW), reaching a maximum output power of 145 mW and a slope efficiency of 12.9%

Název v anglickém jazyce

Crystal growth, optical spectroscopy, and continuous-wave laser operation of co-doped (Ho, Tm):KLu(WO4)2 monoclinic crystals

Popis výsledku anglicky

We report on the crystal growth, optical spectroscopy, and room-temperature continuous-wave laser generation around 2 μm with co-doped Ho, Tm∶KLu WO42 monoclinic crystals. Co-doped crystals at different doping levels were grown by the top-seeded solution growth slow-cooling method. We characterized the spectroscopy of Ho and Tm ions in KLuW in terms of polarized optical absorption, photoluminescence, and lifetime measurements. Continuous-wave laser operation at room-temperature at a wavelength of 2.06 μm was achieved with several crystals at different co-doping levels, establishing that the optimum doping ratio is 5.29 × 1019 at:∕cm3 for Ho and 3.10 × 1020 at:∕cm3 for Tm (0.5 at. %Ho, 5.0 at. %Tm:KLuW), reaching a maximum output power of 145 mW and a slope efficiency of 12.9%

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

10306 - Optics (including laser optics and quantum optics)

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2014

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of the Optical Society of America. B

ISSN

0740-3224

e-ISSN

—

Svazek periodika

31

Číslo periodika v rámci svazku

7

Stát vydavatele periodika

US - Spojené státy americké

Počet stran výsledku

7

Strana od-do

1415-1421

Kód UT WoS článku

000338931700002

EID výsledku v databázi Scopus

2-s2.0-84903695490