The magnetic and neutron diffraction studies of La1-xSrxMnO3 nanoparticles prepared via molten salt synthesis

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F15%3A00435369" target="_blank" >RIV/68378271:_____/15:00435369 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/68407700:21340/15:00226059

Výsledek na webu

<a href="http://dx.doi.org/10.1016/j.jssc.2014.10.024" target="_blank" >http://dx.doi.org/10.1016/j.jssc.2014.10.024</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.jssc.2014.10.024" target="_blank" >10.1016/j.jssc.2014.10.024</a>

Jazyk výsledku

angličtina

Název v původním jazyce

The magnetic and neutron diffraction studies of La1-xSrxMnO3 nanoparticles prepared via molten salt synthesis

Popis výsledku v původním jazyce

Series ofsingle-phase La1-xSrxMnO3 nanoparticles (x0.25 0.47)with the size of about 50nm was prepared in molten NaNO2. TEM evidenced well dispersed particles that are not interconnected by sintering bridges in contrast to traditional products.Interestingly,some reduction of the perovskite cell volume, particularly at higherSr contents,was detected by XRD.Moreover,reduced magnetization and decreased Curie temperature in comparison to sol?gel samples were observed.Neutron diffraction analysis of the as-prepared nanoparticles and several comparative samples with x=0.37 indicated that the anomalous behavior of studied particles probably originate in the overdoped outer shell.The overdoping might result from both the surface oxygen chemisorption and from anincreased Sr concentration in the shell.

Název v anglickém jazyce

The magnetic and neutron diffraction studies of La1-xSrxMnO3 nanoparticles prepared via molten salt synthesis

Popis výsledku anglicky

Series ofsingle-phase La1-xSrxMnO3 nanoparticles (x0.25 0.47)with the size of about 50nm was prepared in molten NaNO2. TEM evidenced well dispersed particles that are not interconnected by sintering bridges in contrast to traditional products.Interestingly,some reduction of the perovskite cell volume, particularly at higherSr contents,was detected by XRD.Moreover,reduced magnetization and decreased Curie temperature in comparison to sol?gel samples were observed.Neutron diffraction analysis of the as-prepared nanoparticles and several comparative samples with x=0.37 indicated that the anomalous behavior of studied particles probably originate in the overdoped outer shell.The overdoping might result from both the surface oxygen chemisorption and from anincreased Sr concentration in the shell.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BM - Fyzika pevných látek a magnetismus

OECD FORD obor

—

Projekt

<a href="/cs/project/GAP108%2F11%2F0807" target="_blank" >GAP108/11/0807: Komplexní magnetické nanočástice s monodisperzními oxidovými jádry a stabilním organickým obalem pro biologický výzkum a biomedicinální aplikace</a><br>

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2015

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of Solid State Chemistry

ISSN

0022-4596

e-ISSN

—

Svazek periodika

221

Číslo periodika v rámci svazku

Jan

Stát vydavatele periodika

US - Spojené státy americké

Počet stran výsledku

9

Strana od-do

364-372

Kód UT WoS článku

000347263700051

EID výsledku v databázi Scopus

—