A low-cost, environment-friendly and solvent-free route for synthesis of AgBr nanoparticles
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F15%3A00448310" target="_blank" >RIV/68378271:_____/15:00448310 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.1016/j.spmi.2015.01.030" target="_blank" >http://dx.doi.org/10.1016/j.spmi.2015.01.030</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.spmi.2015.01.030" target="_blank" >10.1016/j.spmi.2015.01.030</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
A low-cost, environment-friendly and solvent-free route for synthesis of AgBr nanoparticles
Popis výsledku v původním jazyce
We report on the synthesis of AgBr nanoparticles average size below 20 nm by from AgNO3 and a thiosemicarbazone ligand, Brcatsc [Brcatsc = 2-bromo-3-phenylpropenalthiosemicarbazone]. Brcatsc was prepared by reacting ?-bromocinnam-aldehyde and thiosemicarbazide (1:1, molar ratio) in hot ethanol characterized by elemental analyses (CHN), FT-IR, 1H NMR spectroscopy and single crystal X-ray diffraction. AgBr nanoparticles were prepared by heating the mixture of AgNO3 and Brcatsc at 600 C for 3 h under aerobic condition, and characterized by X-ray powder diffraction (XRD), scanning electron microsco py (SEM) and transmission electron microscopy (TEM). The XRD pattern clearly indicates the formation of AgBr nanoparticles while SEM and TEM results reveal their uniformity and purity.
Název v anglickém jazyce
A low-cost, environment-friendly and solvent-free route for synthesis of AgBr nanoparticles
Popis výsledku anglicky
We report on the synthesis of AgBr nanoparticles average size below 20 nm by from AgNO3 and a thiosemicarbazone ligand, Brcatsc [Brcatsc = 2-bromo-3-phenylpropenalthiosemicarbazone]. Brcatsc was prepared by reacting ?-bromocinnam-aldehyde and thiosemicarbazide (1:1, molar ratio) in hot ethanol characterized by elemental analyses (CHN), FT-IR, 1H NMR spectroscopy and single crystal X-ray diffraction. AgBr nanoparticles were prepared by heating the mixture of AgNO3 and Brcatsc at 600 C for 3 h under aerobic condition, and characterized by X-ray powder diffraction (XRD), scanning electron microsco py (SEM) and transmission electron microscopy (TEM). The XRD pattern clearly indicates the formation of AgBr nanoparticles while SEM and TEM results reveal their uniformity and purity.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
BM - Fyzika pevných látek a magnetismus
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GA14-03276S" target="_blank" >GA14-03276S: Nesférické efekty a jejich využití pro statisticky korektní analýzu krystalových struktur</a><br>
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2015
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Superlattices and Microstructures
ISSN
0749-6036
e-ISSN
—
Svazek periodika
82
Číslo periodika v rámci svazku
Jun
Stát vydavatele periodika
GB - Spojené království Velké Británie a Severního Irska
Počet stran výsledku
8
Strana od-do
18-25
Kód UT WoS článku
000357141400003
EID výsledku v databázi Scopus
2-s2.0-84923819897