Effect of applied tensile stress on the hysteresis curve and magnetic domain structure of grain-oriented transverse Fe-3%Si steel

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F15%3A00448400" target="_blank" >RIV/68378271:_____/15:00448400 - isvavai.cz</a>

Výsledek na webu

<a href="http://dx.doi.org/10.1016/j.jmmm.2015.03.040" target="_blank" >http://dx.doi.org/10.1016/j.jmmm.2015.03.040</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.jmmm.2015.03.040" target="_blank" >10.1016/j.jmmm.2015.03.040</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Effect of applied tensile stress on the hysteresis curve and magnetic domain structure of grain-oriented transverse Fe-3%Si steel

Popis výsledku v původním jazyce

The effect of an elastic applied tensile stress on the quasistatic hysteresis curve and domain structure in conventional (110) [001] Fe-3%Si steel, cut transversely to the rolling direction, is studied. The magnetic domains and magnetization processes were observed by longitudinal Kerr microscopy at different levels of stress. It is shown that above 8 MPa the bulk hysteresis loop can be described with a good accuracy by the action of an effective field, which is the product of the stress and a functionof magnetization. Domain observation reveals that the reasons for the effective field are demagnetizing fields due to the disappearance of supplementary domains at low applied field and the formation of different domain systems in different grains at lowand moderate fields.

Název v anglickém jazyce

Effect of applied tensile stress on the hysteresis curve and magnetic domain structure of grain-oriented transverse Fe-3%Si steel

Popis výsledku anglicky

The effect of an elastic applied tensile stress on the quasistatic hysteresis curve and domain structure in conventional (110) [001] Fe-3%Si steel, cut transversely to the rolling direction, is studied. The magnetic domains and magnetization processes were observed by longitudinal Kerr microscopy at different levels of stress. It is shown that above 8 MPa the bulk hysteresis loop can be described with a good accuracy by the action of an effective field, which is the product of the stress and a functionof magnetization. Domain observation reveals that the reasons for the effective field are demagnetizing fields due to the disappearance of supplementary domains at low applied field and the formation of different domain systems in different grains at lowand moderate fields.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BM - Fyzika pevných látek a magnetismus

OECD FORD obor

—

Projekt

<a href="/cs/project/GA13-18993S" target="_blank" >GA13-18993S: Vývoj a testování nových soustav pro měření magnetického Barkhausenova šumu při kontrolovaných magnetizačních podmínkách</a><br>

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2015

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of Magnetism and Magnetic Materials

ISSN

0304-8853

e-ISSN

—

Svazek periodika

385

Číslo periodika v rámci svazku

Jul

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

10

Strana od-do

358-367

Kód UT WoS článku

000352489100055

EID výsledku v databázi Scopus

2-s2.0-84925004297