Influence of diamond and graphite bonds on mechanical properties of DLC thin films
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F15%3A00449703" target="_blank" >RIV/68378271:_____/15:00449703 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/68407700:21460/15:00227531 RIV/68407700:21220/15:00227531
Výsledek na webu
<a href="http://dx.doi.org/10.1088/1742-6596/594/1/012008" target="_blank" >http://dx.doi.org/10.1088/1742-6596/594/1/012008</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1088/1742-6596/594/1/012008" target="_blank" >10.1088/1742-6596/594/1/012008</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Influence of diamond and graphite bonds on mechanical properties of DLC thin films
Popis výsledku v původním jazyce
Mechanical properties of diamond-like carbon thin films with various ratios of sp3/sp2 bonds were studied. The films were prepared in argon atmosphere (0.25 Pa) by laser deposition method for laser energy densities from 4 J.cm-2 to 14 J.cm-2. The sp2 andsp3 bonds were calculated by X-ray photoelectron spectroscopy. Films contained sp3 bonds up to 70 %. Surface properties as roughness and atomic force microscopy topology were measured. Hardness (and reduced Young's modulus) were determined by nanoindentation and reached of 30 GPa (203 GPa). Films adhesion was studied using scratch test and was up to 12 N for biomedical alloy (titanium substrates - Ti-6Al-4V). Relations among deposition conditions and measured properties are presented.
Název v anglickém jazyce
Influence of diamond and graphite bonds on mechanical properties of DLC thin films
Popis výsledku anglicky
Mechanical properties of diamond-like carbon thin films with various ratios of sp3/sp2 bonds were studied. The films were prepared in argon atmosphere (0.25 Pa) by laser deposition method for laser energy densities from 4 J.cm-2 to 14 J.cm-2. The sp2 andsp3 bonds were calculated by X-ray photoelectron spectroscopy. Films contained sp3 bonds up to 70 %. Surface properties as roughness and atomic force microscopy topology were measured. Hardness (and reduced Young's modulus) were determined by nanoindentation and reached of 30 GPa (203 GPa). Films adhesion was studied using scratch test and was up to 12 N for biomedical alloy (titanium substrates - Ti-6Al-4V). Relations among deposition conditions and measured properties are presented.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
BM - Fyzika pevných látek a magnetismus
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GA13-33056S" target="_blank" >GA13-33056S: Charakterizace tenkých termoelektrických vrstev a multi-vrstevnatých struktur pomocí rastrovacího termálního mikroskopu a Harmanovy metody.</a><br>
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2015
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Journal of Physics Conference Series, Vol. 594
ISBN
—
ISSN
1742-6588
e-ISSN
—
Počet stran výsledku
6
Strana od-do
—
Název nakladatele
IOP PUBLISHING LTD
Místo vydání
Bristol
Místo konání akce
Sofia
Datum konání akce
14. 7. 2014
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
000352084500007