Thin polycrystalline diamond films protecting zirconium alloys surfaces: from technology to layer analysis and application in nuclear facilities

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F15%3A00454671" target="_blank" >RIV/68378271:_____/15:00454671 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/68407700:21340/15:00238940 RIV/68407700:21220/15:00238940 RIV/60461373:22320/15:43900060

Výsledek na webu

<a href="http://dx.doi.org/10.1016/j.apsusc.2015.10.117" target="_blank" >http://dx.doi.org/10.1016/j.apsusc.2015.10.117</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.apsusc.2015.10.117" target="_blank" >10.1016/j.apsusc.2015.10.117</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Thin polycrystalline diamond films protecting zirconium alloys surfaces: from technology to layer analysis and application in nuclear facilities

Popis výsledku v původním jazyce

Zirconium alloys can be effectively protected against corrosion by polycrystalline diamond (PCD) layers grown in microwave plasma enhanced linear antenna chemical vapor deposition apparatus. Standard and hot steam oxidized PCD layers grown on Zircaloy2 surfaces were examined and the specific impact of polycrystalline Zr substrate surface on PCD layer properties was investigated. It was found that the presence of the PCD coating blocks hydrogen diffusion into the Zircaloy2 surface and protects Zircaloy2material from degradation. PCD anticorrosion protection of Zircaloy2 can significantly prolong life of Zircaloy2 material in nuclear reactors even at temperatures above Zr phase transition temperatures.

Název v anglickém jazyce

Thin polycrystalline diamond films protecting zirconium alloys surfaces: from technology to layer analysis and application in nuclear facilities

Popis výsledku anglicky

Zirconium alloys can be effectively protected against corrosion by polycrystalline diamond (PCD) layers grown in microwave plasma enhanced linear antenna chemical vapor deposition apparatus. Standard and hot steam oxidized PCD layers grown on Zircaloy2 surfaces were examined and the specific impact of polycrystalline Zr substrate surface on PCD layer properties was investigated. It was found that the presence of the PCD coating blocks hydrogen diffusion into the Zircaloy2 surface and protects Zircaloy2material from degradation. PCD anticorrosion protection of Zircaloy2 can significantly prolong life of Zircaloy2 material in nuclear reactors even at temperatures above Zr phase transition temperatures.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JI - Kompositní materiály

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2015

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Applied Surface Science

ISSN

0169-4332

e-ISSN

—

Svazek periodika

359

Číslo periodika v rámci svazku

Dec

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

8

Strana od-do

621-628

Kód UT WoS článku

000366220600083

EID výsledku v databázi Scopus

—