Evolution of internal stresses during cyclic superelastic deformation of NiTi investigated by X-ray synchrotron diffraction

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F15%3A00456634" target="_blank" >RIV/68378271:_____/15:00456634 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/68407700:21340/15:00235344

Výsledek na webu

<a href="http://dx.doi.org/10.1016/j.matpr.2015.07.386" target="_blank" >http://dx.doi.org/10.1016/j.matpr.2015.07.386</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.matpr.2015.07.386" target="_blank" >10.1016/j.matpr.2015.07.386</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Evolution of internal stresses during cyclic superelastic deformation of NiTi investigated by X-ray synchrotron diffraction

Popis výsledku v původním jazyce

Cyclic tensile superelastic deformation of NiTi was investigated using high resolution in-situ synchrotron x-ray diffraction method. Diffraction patterns were recorded under applied stress prior and after the stress induced martensitic transformation, analyzed and interpreted in view of the evolution of microstructure in the transforming polycrystal. A simple bicrystal scheme of the polycrystal transformation is used to rationalize the experimental evidence on microstructure evolution during cycling. It is claimed that the instability of cyclic superelastic response of NiTi is due to the gradual rise of internal stresses originating from the accumulation of plastic deformation accompanying the martensitic transformation in constrained polycrystalline environment.

Název v anglickém jazyce

Evolution of internal stresses during cyclic superelastic deformation of NiTi investigated by X-ray synchrotron diffraction

Popis výsledku anglicky

Cyclic tensile superelastic deformation of NiTi was investigated using high resolution in-situ synchrotron x-ray diffraction method. Diffraction patterns were recorded under applied stress prior and after the stress induced martensitic transformation, analyzed and interpreted in view of the evolution of microstructure in the transforming polycrystal. A simple bicrystal scheme of the polycrystal transformation is used to rationalize the experimental evidence on microstructure evolution during cycling. It is claimed that the instability of cyclic superelastic response of NiTi is due to the gradual rise of internal stresses originating from the accumulation of plastic deformation accompanying the martensitic transformation in constrained polycrystalline environment.

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2015

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Materials Today: Proceedings ICOMAT 2014

ISBN

—

ISSN

2214-7853

e-ISSN

—

Počet stran výsledku

4

Strana od-do

731-734

Název nakladatele

Elsevier Ltd

Místo vydání

Amsterdam

Místo konání akce

Bilbao

Datum konání akce

6. 7. 2014

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—