Calcium-induced cation ordering and large resistivity decrease in Pr0.3CoO2

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F16%3A00466138" target="_blank" >RIV/68378271:_____/16:00466138 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/61388980:_____/16:00466138

Výsledek na webu

<a href="http://dx.doi.org/10.1016/j.jpcs.2016.04.012" target="_blank" >http://dx.doi.org/10.1016/j.jpcs.2016.04.012</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.jpcs.2016.04.012" target="_blank" >10.1016/j.jpcs.2016.04.012</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Calcium-induced cation ordering and large resistivity decrease in Pr0.3CoO2

Popis výsledku v původním jazyce

Structure of layered cobaltates Pr0.3CoO2 and (PrCa)0.3CoO2 were investigated by electron diffraction tomography and powder X-ray diffraction. The effect of the calcium substitution on thermoelectric properties was evaluated. The structure consists of hexagonal sheets of edge-sharing CoO6 octahedra interleaved by cationic monolayers. The cations form a 2-dimensional a3a3 superstructure in the a–b plane. While Pr0.3CoO2 showed no layer order in the [001] direction, introduction of calcium resulted in the formation of a superstructure spanning over six cationic layers along the [001]. This superstructure model appears to be valid also for the description of the superstructures of CaxCoO2 and SrxCoO2 with x about 1/3.

Název v anglickém jazyce

Calcium-induced cation ordering and large resistivity decrease in Pr0.3CoO2

Popis výsledku anglicky

Structure of layered cobaltates Pr0.3CoO2 and (PrCa)0.3CoO2 were investigated by electron diffraction tomography and powder X-ray diffraction. The effect of the calcium substitution on thermoelectric properties was evaluated. The structure consists of hexagonal sheets of edge-sharing CoO6 octahedra interleaved by cationic monolayers. The cations form a 2-dimensional a3a3 superstructure in the a–b plane. While Pr0.3CoO2 showed no layer order in the [001] direction, introduction of calcium resulted in the formation of a superstructure spanning over six cationic layers along the [001]. This superstructure model appears to be valid also for the description of the superstructures of CaxCoO2 and SrxCoO2 with x about 1/3.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BM - Fyzika pevných látek a magnetismus

OECD FORD obor

—

Projekt

<a href="/cs/project/GA13-03708S" target="_blank" >GA13-03708S: Elektrický transport a magnetismus v nových vrstevnatých kobaltátech se vzácnými zeminami</a><br>

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2016

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of Physics and Chemistry of Solids

ISSN

0022-3697

e-ISSN

—

Svazek periodika

96-97

Číslo periodika v rámci svazku

Sep

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

7

Strana od-do

10-16

Kód UT WoS článku

000378960700002

EID výsledku v databázi Scopus

2-s2.0-84966441027