TEM phase analysis of NiTi shape memory alloy prepared by self-propagating high-temperature synthesis
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F17%3A00470162" target="_blank" >RIV/68378271:_____/17:00470162 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/61389005:_____/17:00470162 RIV/68407700:21340/17:00337250
Výsledek na webu
<a href="http://dx.doi.org/10.1080/2374068X.2016.1247338" target="_blank" >http://dx.doi.org/10.1080/2374068X.2016.1247338</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1080/2374068X.2016.1247338" target="_blank" >10.1080/2374068X.2016.1247338</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
TEM phase analysis of NiTi shape memory alloy prepared by self-propagating high-temperature synthesis
Popis výsledku v původním jazyce
The effect of annealing a Ni–48at.%Ti alloy prepared by selfpropagation high-temperature synthesis (SHS) by means of transmission electron microscopy (TEM) was studied. The alloy in the as-sintered condition shows the presence of B2 NiTi matrix, relatively large particles (2–100 μm) of cubic NiTi2 phase and very fine densely distributed particles of rhombohedral Ni4Ti3 phase. The phase fractions were determined by the Rietveld refinement of neutron diffraction. Twelve-hour annealing at 1000 °C leads to coarsening of Ni4Ti3 particles. Slow furnace cooling from the annealing temperature results in a transformation of the rhombohedral Ni4Ti3 phase to a metastable Ni3Ti2 phase with cubic symmetry. Its particles, coherent with the B2 matrix, have the form of thin oval platelets with lenticular cross-section.
Název v anglickém jazyce
TEM phase analysis of NiTi shape memory alloy prepared by self-propagating high-temperature synthesis
Popis výsledku anglicky
The effect of annealing a Ni–48at.%Ti alloy prepared by selfpropagation high-temperature synthesis (SHS) by means of transmission electron microscopy (TEM) was studied. The alloy in the as-sintered condition shows the presence of B2 NiTi matrix, relatively large particles (2–100 μm) of cubic NiTi2 phase and very fine densely distributed particles of rhombohedral Ni4Ti3 phase. The phase fractions were determined by the Rietveld refinement of neutron diffraction. Twelve-hour annealing at 1000 °C leads to coarsening of Ni4Ti3 particles. Slow furnace cooling from the annealing temperature results in a transformation of the rhombohedral Ni4Ti3 phase to a metastable Ni3Ti2 phase with cubic symmetry. Its particles, coherent with the B2 matrix, have the form of thin oval platelets with lenticular cross-section.
Klasifikace
Druh
J<sub>ost</sub> - Ostatní články v recenzovaných periodicích
CEP obor
—
OECD FORD obor
10302 - Condensed matter physics (including formerly solid state physics, supercond.)
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2017
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Advances in Materials and Processing Technologies
ISSN
2374-068X
e-ISSN
—
Svazek periodika
3
Číslo periodika v rámci svazku
1
Stát vydavatele periodika
GB - Spojené království Velké Británie a Severního Irska
Počet stran výsledku
12
Strana od-do
58-69
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—