Corrosion protection of zirconium surface based on Heusler alloy

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F17%3A00478343" target="_blank" >RIV/68378271:_____/17:00478343 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/60461373:22320/17:43913776

Výsledek na webu

<a href="http://dx.doi.org/10.1515/pac-2016-1030" target="_blank" >http://dx.doi.org/10.1515/pac-2016-1030</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1515/pac-2016-1030" target="_blank" >10.1515/pac-2016-1030</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Corrosion protection of zirconium surface based on Heusler alloy

Popis výsledku v původním jazyce

Fe and Si films were tested as corrosion protection layers for Zr in nuclear industry applications. Corrosion experiments were carried out in autoclave conditions with in-situ Electrochemical Impedance spectroscopy. A clean Zr surface is characteristic with disposition to disorder and rough morphology demonstrated in facets, steps or terraces. Upon deposition of Fe and Si atoms in amounts in the order of single monolayers and subsequent annealing at 400 °C, the original (1 × 1) Zr surface structure rearranges into (2 √ 3 × 2 √ 3)R30°. Corrosion experiments show that a thicker Si overlayer successfully suppresses oxygen uptake of the underlying Zr material by forming a diffusion barrier. The barrier effect of the films was also confirmed for hydrogen.n

Název v anglickém jazyce

Corrosion protection of zirconium surface based on Heusler alloy

Popis výsledku anglicky

Fe and Si films were tested as corrosion protection layers for Zr in nuclear industry applications. Corrosion experiments were carried out in autoclave conditions with in-situ Electrochemical Impedance spectroscopy. A clean Zr surface is characteristic with disposition to disorder and rough morphology demonstrated in facets, steps or terraces. Upon deposition of Fe and Si atoms in amounts in the order of single monolayers and subsequent annealing at 400 °C, the original (1 × 1) Zr surface structure rearranges into (2 √ 3 × 2 √ 3)R30°. Corrosion experiments show that a thicker Si overlayer successfully suppresses oxygen uptake of the underlying Zr material by forming a diffusion barrier. The barrier effect of the films was also confirmed for hydrogen.n

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

20505 - Composites (including laminates, reinforced plastics, cermets, combined natural and synthetic fibre fabrics; filled composites)

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2017

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Pure and Applied Chemistry

ISSN

0033-4545

e-ISSN

—

Svazek periodika

89

Číslo periodika v rámci svazku

4

Stát vydavatele periodika

US - Spojené státy americké

Počet stran výsledku

11

Strana od-do

553-563

Kód UT WoS článku

000403319800016

EID výsledku v databázi Scopus

2-s2.0-85019393635