Powder-metallurgy preparation of NiTi shape-memory alloy using mechanical alloying and spark-plasma sintering.
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F17%3A00479483" target="_blank" >RIV/68378271:_____/17:00479483 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/61389021:_____/17:00479483 RIV/60461373:22310/17:43915381
Výsledek na webu
<a href="http://dx.doi.org/10.17222/mit.2016.011" target="_blank" >http://dx.doi.org/10.17222/mit.2016.011</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.17222/mit.2016.011" target="_blank" >10.17222/mit.2016.011</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Powder-metallurgy preparation of NiTi shape-memory alloy using mechanical alloying and spark-plasma sintering.
Popis výsledku v původním jazyce
In this work a combination of mechanical alloying and spark-plasma sintering was tested as a promising route for the preparation of a nanocrystalline NiTi shape-memory alloy. The mechanism of mechanical alloying was investigated. Results revealed that the Ti2Ni phase forms preferentially, being followed by the NiTi phase (austenite B2 structure) and a small amount of Ni3Ti. During spark-plasma sintering, only minor changes occurred in the phase composition, i.e., precipitation of the Ni4Ti3 phase and the partial transformation of NiTi to monoclinic martensite. The selected technology leads to a very high compression strength (approx. 2300 MPa), but also high brittleness.
Název v anglickém jazyce
Powder-metallurgy preparation of NiTi shape-memory alloy using mechanical alloying and spark-plasma sintering.
Popis výsledku anglicky
In this work a combination of mechanical alloying and spark-plasma sintering was tested as a promising route for the preparation of a nanocrystalline NiTi shape-memory alloy. The mechanism of mechanical alloying was investigated. Results revealed that the Ti2Ni phase forms preferentially, being followed by the NiTi phase (austenite B2 structure) and a small amount of Ni3Ti. During spark-plasma sintering, only minor changes occurred in the phase composition, i.e., precipitation of the Ni4Ti3 phase and the partial transformation of NiTi to monoclinic martensite. The selected technology leads to a very high compression strength (approx. 2300 MPa), but also high brittleness.
Klasifikace
Druh
J<sub>imp</sub> - Článek v periodiku v databázi Web of Science
CEP obor
—
OECD FORD obor
20501 - Materials engineering
Návaznosti výsledku
Projekt
<a href="/cs/project/GA14-03044S" target="_blank" >GA14-03044S: Příprava slitin NiTi s tvarovou pamětí reaktivní sintrací</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2017
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Materials and Technology
ISSN
1580-2949
e-ISSN
—
Svazek periodika
51
Číslo periodika v rámci svazku
1
Stát vydavatele periodika
SI - Slovinská republika
Počet stran výsledku
4
Strana od-do
141-144
Kód UT WoS článku
000396592900022
EID výsledku v databázi Scopus
2-s2.0-85027448989