Growth of LiF/LiBaF3 eutectic scintillator crystals and their optical properties
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F17%3A00483156" target="_blank" >RIV/68378271:_____/17:00483156 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.1007/s10853-017-0815-1" target="_blank" >http://dx.doi.org/10.1007/s10853-017-0815-1</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1007/s10853-017-0815-1" target="_blank" >10.1007/s10853-017-0815-1</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Growth of LiF/LiBaF3 eutectic scintillator crystals and their optical properties
Popis výsledku v původním jazyce
LiF/LiBaF3 can have higher cross section of thermal-neutron capture compared with LiBaF3. In this study, LiF (82.5 mol%) and (Ba1-x REx)F2 (17.5 mol%, RE = Ce and Eu, x = 0.002) eutectic crystals, LiF/RE:LiBaF3, were grown by the micropulling down method with different pulling rates (growth rate) in order to observe the eutectic structure. LiF/Ce:LiBaF3 excited by 5.5-MeV alpha rays had a broad peak at *350 nm correspondingto 5d–4f transition of Ce3+. On the other hand, LiF/Eu:LiBaF3 had two scintillation processes: a sharp emission was originated from 6P7/2 - sup>8S7/2 transitions in the 4f electronic configuration of Eu2+ at 360 nm, and a broad one was attributed to Eu2+ trapped exciton recombination at 400–450 nm.n
Název v anglickém jazyce
Growth of LiF/LiBaF3 eutectic scintillator crystals and their optical properties
Popis výsledku anglicky
LiF/LiBaF3 can have higher cross section of thermal-neutron capture compared with LiBaF3. In this study, LiF (82.5 mol%) and (Ba1-x REx)F2 (17.5 mol%, RE = Ce and Eu, x = 0.002) eutectic crystals, LiF/RE:LiBaF3, were grown by the micropulling down method with different pulling rates (growth rate) in order to observe the eutectic structure. LiF/Ce:LiBaF3 excited by 5.5-MeV alpha rays had a broad peak at *350 nm correspondingto 5d–4f transition of Ce3+. On the other hand, LiF/Eu:LiBaF3 had two scintillation processes: a sharp emission was originated from 6P7/2 - sup>8S7/2 transitions in the 4f electronic configuration of Eu2+ at 360 nm, and a broad one was attributed to Eu2+ trapped exciton recombination at 400–450 nm.n
Klasifikace
Druh
J<sub>imp</sub> - Článek v periodiku v databázi Web of Science
CEP obor
—
OECD FORD obor
10302 - Condensed matter physics (including formerly solid state physics, supercond.)
Návaznosti výsledku
Projekt
—
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2017
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Journal of Materials Science
ISSN
0022-2461
e-ISSN
—
Svazek periodika
52
Číslo periodika v rámci svazku
10
Stát vydavatele periodika
US - Spojené státy americké
Počet stran výsledku
6
Strana od-do
5531-5536
Kód UT WoS článku
000395206400007
EID výsledku v databázi Scopus
2-s2.0-85010976474