Effect of Reaction Atmosphere and Heating Rate during Reactive Sintering of Ni-Ti Intermetallics
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F17%3A00509859" target="_blank" >RIV/68378271:_____/17:00509859 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/68407700:21340/17:00319392
Výsledek na webu
<a href="http://dx.doi.org/10.1016/j.proeng.2017.04.139" target="_blank" >http://dx.doi.org/10.1016/j.proeng.2017.04.139</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.proeng.2017.04.139" target="_blank" >10.1016/j.proeng.2017.04.139</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Effect of Reaction Atmosphere and Heating Rate during Reactive Sintering of Ni-Ti Intermetallics
Popis výsledku v původním jazyce
The effect of reaction atmosphere and heating rate during reactive sintering of nickel and titanium powder blend (Ni: 52 at.%, particle size <150 μm, >99.99% purity, Ti: 48 at.%, particle size <44 μm, >99.5% purity) were studied. The powder mixtures were uniaxially compressed under pressure of 637 MPa and sintered at temperatures 500, 650, 900 and 1100 °C in air, vacuum, argon and nitrogen atmospheres. Two heating rates were applied: 200 and >300 K.min-1. The results show that a significant effect of reaction atmosphere in terms of the quantity of the Ti2Ni phase applies especially at very high heating rate. In terms of phase morphology, oxygen causes refinement of the structure, regardless of heating rate.n
Název v anglickém jazyce
Effect of Reaction Atmosphere and Heating Rate during Reactive Sintering of Ni-Ti Intermetallics
Popis výsledku anglicky
The effect of reaction atmosphere and heating rate during reactive sintering of nickel and titanium powder blend (Ni: 52 at.%, particle size <150 μm, >99.99% purity, Ti: 48 at.%, particle size <44 μm, >99.5% purity) were studied. The powder mixtures were uniaxially compressed under pressure of 637 MPa and sintered at temperatures 500, 650, 900 and 1100 °C in air, vacuum, argon and nitrogen atmospheres. Two heating rates were applied: 200 and >300 K.min-1. The results show that a significant effect of reaction atmosphere in terms of the quantity of the Ti2Ni phase applies especially at very high heating rate. In terms of phase morphology, oxygen causes refinement of the structure, regardless of heating rate.n
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
—
OECD FORD obor
10302 - Condensed matter physics (including formerly solid state physics, supercond.)
Návaznosti výsledku
Projekt
—
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2017
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Procedia Engineering, vol. 184
ISBN
—
ISSN
1877-7058
e-ISSN
—
Počet stran výsledku
6
Strana od-do
681-686
Název nakladatele
Elsevier Ltd.
Místo vydání
Amsterdam
Místo konání akce
Kuala Lumpur
Datum konání akce
8. 11. 2016
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
000414778400082