Crystal growth, low-temperature spectroscopy and multi-watt laser operation of Yb:Ca3NbGa3Si2O14

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F18%3A00492541" target="_blank" >RIV/68378271:_____/18:00492541 - isvavai.cz</a>

Výsledek na webu

<a href="http://dx.doi.org/10.1016/j.jlumin.2018.01.004" target="_blank" >http://dx.doi.org/10.1016/j.jlumin.2018.01.004</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.jlumin.2018.01.004" target="_blank" >10.1016/j.jlumin.2018.01.004</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Crystal growth, low-temperature spectroscopy and multi-watt laser operation of Yb:Ca3NbGa3Si2O14

Popis výsledku v původním jazyce

We report on the crystal growth, structure, room- and low-temperature (6 K) absorption and emission spectroscopy of a 3 at% Yb3+-doped trigonal ordered langasite-type silicate crystal, Ca3NbGa3Si2O14 (Yb: CNGS). The Rietveld refinement data are presented. Absorption, stimulated-emission and gain cross-sections are determined for the Yb3+ ion in CNGS for p and s polarizations. The maximum stimulated emission cross-section amounts to sigma(SE) = 0.97 x 10(-20) cm(-2) at 10(14) nm (sigma-polarization). The Stark splitting of the Yb3+ multiplets is resolved. Microchip laser operation is obtained with both a-cut and c-cut 3 at% Yb: CNGS samples under endpumping at 976 nm by a Volume Bragg Grating-stabilized diode laser. For the latter cut, the maximum output power reaches 7.61 W at 1048-1060 nm with a slope efficiency of 59%. By varying the output coupling, multiwatt emission over a 50 nm-broad spectral range is achieved.

Název v anglickém jazyce

Crystal growth, low-temperature spectroscopy and multi-watt laser operation of Yb:Ca3NbGa3Si2O14

Popis výsledku anglicky

We report on the crystal growth, structure, room- and low-temperature (6 K) absorption and emission spectroscopy of a 3 at% Yb3+-doped trigonal ordered langasite-type silicate crystal, Ca3NbGa3Si2O14 (Yb: CNGS). The Rietveld refinement data are presented. Absorption, stimulated-emission and gain cross-sections are determined for the Yb3+ ion in CNGS for p and s polarizations. The maximum stimulated emission cross-section amounts to sigma(SE) = 0.97 x 10(-20) cm(-2) at 10(14) nm (sigma-polarization). The Stark splitting of the Yb3+ multiplets is resolved. Microchip laser operation is obtained with both a-cut and c-cut 3 at% Yb: CNGS samples under endpumping at 976 nm by a Volume Bragg Grating-stabilized diode laser. For the latter cut, the maximum output power reaches 7.61 W at 1048-1060 nm with a slope efficiency of 59%. By varying the output coupling, multiwatt emission over a 50 nm-broad spectral range is achieved.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

10306 - Optics (including laser optics and quantum optics)

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2018

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of Luminescence

ISSN

0022-2313

e-ISSN

—

Svazek periodika

197

Číslo periodika v rámci svazku

May

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

8

Strana od-do

90-97

Kód UT WoS článku

000425996400013

EID výsledku v databázi Scopus

2-s2.0-85041489568