Comparative study of GdLu2Al2Ga3O12:Ce and GdY2Al2Ga3O12:Ce scintillation crystals for gamma-ray detection
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F18%3A00493049" target="_blank" >RIV/68378271:_____/18:00493049 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.1109/TNS.2018.2809563" target="_blank" >http://dx.doi.org/10.1109/TNS.2018.2809563</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1109/TNS.2018.2809563" target="_blank" >10.1109/TNS.2018.2809563</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Comparative study of GdLu2Al2Ga3O12:Ce and GdY2Al2Ga3O12:Ce scintillation crystals for gamma-ray detection
Popis výsledku v původním jazyce
The scintillation characteristics of Czochralski-grown GdLu2Al2Ga3O12:Ce and GdY2Al2Ga3O12:Ce single crystals were compared for gamma-ray detection. At 662-keV gamma-rays, light yield (LY) of 30700 photons/MeV obtained for GdLu2Al2Ga3O12:Ce is higher than that of 27 200 photons/MeV obtained for GdY2Al2Ga3O12:Ce, while its energy resolution is inferior (14% versus 10.6%) due to a larger nonproportionality of LY. Scintillation decays were measured using the time-correlated single photon counting technique. A fast component decay time of 48 ns with relative intensity of 71% obtained for GdLu2Al2Ga3O12:Ce is superior to that of 106 ns (57%) for GdY2Al2Ga3O12:Ce. The coincidence time spectrum was measured in reference to a fast BaF2 scintillator, and coincidence time resolution was discussed.
Název v anglickém jazyce
Comparative study of GdLu2Al2Ga3O12:Ce and GdY2Al2Ga3O12:Ce scintillation crystals for gamma-ray detection
Popis výsledku anglicky
The scintillation characteristics of Czochralski-grown GdLu2Al2Ga3O12:Ce and GdY2Al2Ga3O12:Ce single crystals were compared for gamma-ray detection. At 662-keV gamma-rays, light yield (LY) of 30700 photons/MeV obtained for GdLu2Al2Ga3O12:Ce is higher than that of 27 200 photons/MeV obtained for GdY2Al2Ga3O12:Ce, while its energy resolution is inferior (14% versus 10.6%) due to a larger nonproportionality of LY. Scintillation decays were measured using the time-correlated single photon counting technique. A fast component decay time of 48 ns with relative intensity of 71% obtained for GdLu2Al2Ga3O12:Ce is superior to that of 106 ns (57%) for GdY2Al2Ga3O12:Ce. The coincidence time spectrum was measured in reference to a fast BaF2 scintillator, and coincidence time resolution was discussed.
Klasifikace
Druh
J<sub>imp</sub> - Článek v periodiku v databázi Web of Science
CEP obor
—
OECD FORD obor
10302 - Condensed matter physics (including formerly solid state physics, supercond.)
Návaznosti výsledku
Projekt
<a href="/cs/project/GA16-15569S" target="_blank" >GA16-15569S: Rychlé tenkovrstvé scintilátory pro 2D-zobrazování s vysokým rozlišením</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2018
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
IEEE Transactions on Nuclear Science
ISSN
0018-9499
e-ISSN
—
Svazek periodika
65
Číslo periodika v rámci svazku
8
Stát vydavatele periodika
US - Spojené státy americké
Počet stran výsledku
4
Strana od-do
2081-2084
Kód UT WoS článku
000442365000016
EID výsledku v databázi Scopus
2-s2.0-85042686550