Scintillation properties of Gd3(Al5-xGax)O12:Ce (x = 2.3, 2.6, 3.0) single crystals

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F18%3A00501256" target="_blank" >RIV/68378271:_____/18:00501256 - isvavai.cz</a>

Výsledek na webu

<a href="http://dx.doi.org/10.1016/j.optmat.2018.05.015" target="_blank" >http://dx.doi.org/10.1016/j.optmat.2018.05.015</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.optmat.2018.05.015" target="_blank" >10.1016/j.optmat.2018.05.015</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Scintillation properties of Gd3(Al5-xGax)O12:Ce (x = 2.3, 2.6, 3.0) single crystals

Popis výsledku v původním jazyce

Scintillation properties of Czochralski-grown Gd3(Al5-xGax)O12:Ce (x = 2.3, 2.6, 3.0) single crystals were investigated. With increasing Ga content in garnet host, the radioluminescence band due to 5d1 → 4f emission transition was blue-shifted due to a decrease in the crystal field splitting of the 5 d levels. At 662 keV γ rays, the LY value of 47,000, 55,100 and 51,900 ph/MeV was obtained for Gd3Al2.7Ga2.3O12:Ce, Gd3Al2.4Ga2.6O12:Ce and Gd3Al2Ga3O12:Ce, respectively. In spite of a lower LY value, Gd3Al2.7Ga2.3O12:Ce shows good energy resolution of 4.1% due to its proportionality of LY. The ratio of LY values under excitation with α- and γ-rays (α/γ ratio) was also determined. The fast component decay time with relative intensity of 146 ns (66%), 142 ns (76%) and 112 ns (76%) was measured in the scintillation decay of Gd3Al2.7Ga2.3O12:Ce, Gd3Al2.4Ga2.6O12:Ce and Gd3Al2Ga3O12:Ce, respectively.

Název v anglickém jazyce

Scintillation properties of Gd3(Al5-xGax)O12:Ce (x = 2.3, 2.6, 3.0) single crystals

Popis výsledku anglicky

Scintillation properties of Czochralski-grown Gd3(Al5-xGax)O12:Ce (x = 2.3, 2.6, 3.0) single crystals were investigated. With increasing Ga content in garnet host, the radioluminescence band due to 5d1 → 4f emission transition was blue-shifted due to a decrease in the crystal field splitting of the 5 d levels. At 662 keV γ rays, the LY value of 47,000, 55,100 and 51,900 ph/MeV was obtained for Gd3Al2.7Ga2.3O12:Ce, Gd3Al2.4Ga2.6O12:Ce and Gd3Al2Ga3O12:Ce, respectively. In spite of a lower LY value, Gd3Al2.7Ga2.3O12:Ce shows good energy resolution of 4.1% due to its proportionality of LY. The ratio of LY values under excitation with α- and γ-rays (α/γ ratio) was also determined. The fast component decay time with relative intensity of 146 ns (66%), 142 ns (76%) and 112 ns (76%) was measured in the scintillation decay of Gd3Al2.7Ga2.3O12:Ce, Gd3Al2.4Ga2.6O12:Ce and Gd3Al2Ga3O12:Ce, respectively.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

10302 - Condensed matter physics (including formerly solid state physics, supercond.)

Projekt

<a href="/cs/project/GA16-15569S" target="_blank" >GA16-15569S: Rychlé tenkovrstvé scintilátory pro 2D-zobrazování s vysokým rozlišením</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2018

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Optical Materials

ISSN

0925-3467

e-ISSN

—

Svazek periodika

81

Číslo periodika v rámci svazku

July

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

7

Strana od-do

23-29

Kód UT WoS článku

000438324400004

EID výsledku v databázi Scopus

2-s2.0-85046741344